Harga Baja VCN

Steel VCN 150

Characteristics
It has high hardenability and is capable of giving good properties in large sections. It is relatively free from temper brittleness and retains useful machinability at relatively high hardness.

Equivalent VCN 150

Thyssen 6582, DIN 34NiCrMo6, ASSAB 705, JIS SMCM 431, AISI 4340

Availability
Round bar

Chemical Composition (%)

C Si Mn P S Ni Cr Mo
0.38–0.43 0.20–0.35 0.60–0.80 0.40 Max 0.040 Max 1.65–2.00 0.70–0.90 0.20-0.30

Mechanical Properties
Hardening Temp : 820 – 850 C
Ouenching Medium : Oil
Hardness as Supplied : 220 – 250 BHN,
Sizes Available : 20mm – 300mm

Applications
Automotive crankshafts and rear axle shafts, aircrafts crankshafts, Connecting Rods, Propeller Hubs, Gears, Drive shafts, Landing gear parts and heavy duty parts of rock drill

Lebih Detail »

Related Machinery Steel:

Iklan

Harga Plat Mild Steel ASTM A-36

Characteristic

Mild Steel Plate, also known as Hot Rolled A36 Steel Plate is a structural quality steel plate used for a large variety of general construction and industrial applications. Mild Steel Plate ASTM A-36 is one of the most commonly used hot rolled general structural steel. Typical carbon steel materials, they are very cheap, excelling in weldability & machinability and they can be subjected to various heat treatments.

Availability
Supplied as plates, sheets, flats, bars, sections, etc.
Plate Thickness: 4.5 mm, 6 mm, 8 mm, 10 mm dan 12 mm
Size: 5′ x 20′ , 6′ x 20′ , 4′ x 8′
Size: Thickness x Width x Length

Specifications
Grade: ASTM A36, AISI A-36
Workability: Easy to Weld, Cut, Form and Machine

Mechanical Properties

  • Density (kg/m3): 7860
  • Young’s Modulus (GPa): 190-210
  • Tensile Strength (MPa): 400 – 510 MPa
  • Yield Strength (MPa): 205-245 MPa
  • Poisson’s ratio: 0.26
  • Brinell Hardness (HB) 160

Equivalents
DIN Equivalents for JIS SS400: 17100 St 44-2
ASTM Equivalents for JIS SS400: ASTM A36, ASTM A283 Grade D
EN Equivalents for JIS SS400: EN S275/ BS 43A

Chemical Composition (%)
Carbon (C), Silicon (Si) and Manganese (Mn) content are not controlled. Phosphorus (P) 0.05% Max and Sulphur (S) 0.05% Max have to controlled below these levels.

Tabel Ukuran & Berat Nominal Plat ASTM A-36:
Product Thickness (mm) Standard Sheet Size Weight per square metre
Mild Steel Plate 3mm 3.00 1200 x 2400mm (1.2 x 2.4m) 23.55
Mild Steel Plate 4mm 4.00 1200 x 2400mm (1.2 x 2.4m) 31.4
Mild Steel Plate 5mm 5.00 1200 x 2400mm (1.2 x 2.4m) 39.25
Mild Steel Plate 6mm 6.00 1200 x 2400mm (1.2 x 2.4m) 47.1
Mild Steel Plate 8mm 8.00 1200 x 2400mm (1.2 x 2.4m) 62.8
Mild Steel Plate 10mm 10.00 1200 x 2400mm (1.2 x 2.4m) 78.5
Mild Steel Plate 12mm 12.00 1200 x 2400mm (1.2 x 2.4m) 94.2
Mild Steel Plate 16mm 16.00 1200 x 2400mm (1.2 x 2.4m) 125.6
Mild Steel Plate 20mm 20.00 1200 x 2400mm (1.2 x 2.4m) 157
Mild Steel Plate 25mm 25.00 1200 x 2400mm (1.2 x 2.4m) 196.25
Melting Point
Melting point of SS400 is 1430 Degree Celsius
Applications:
base plates, gussets, liners, road plates, trench covers, etc.

Related Carbon Steel:

Harga AISI 1045 Steel

AISI 1045 Steel Roundbar

Characteristic
AISI 1045 Steel is a medium strength steel. Suitable for shafts studs, keys etc. Available as rolled or normalised. Supplied as square bar, or round bar or flat. They are excelling in weldability & machinability , and they can be subjected to various heat treatments. Based on JIS G 4051-2009
AISI 1045 Steel Standard and Grade: JIS S45C DIN1.1151 is typical for flame hardening, and can produce a surface hardness of 500 BHN to a depth of 0.10 in this applies particularly to shafts and gears

Availability
Round bar, Flat

Size

Round Bar: Φ 3.2 – 400mm

Flat: 10 – 90 mm & 205 – 305mm or

Mechanical Properties
* Density (kg/m3) 7700-8030
* Young’s Modulus (GPa) 190-210
* Tensile Strength (Mpa) 569 (Standard) 686 (Quenching, Tempering)
* Yield Strength (Mpa) 343 (Standard) 490 (Quenching, Tempering)
* Poisson’s ratio 0.27-0.30

Hardness
Brinell Hardness (HB) 160-220 (Annealed)

Equivalents
DIN Equivalents for JIS S45C
C45, CK45, CF45, CQ45

ASTM Equivalents for JIS S45C
ASTM A29 , ASTM A510 , ASTM A519 , ASTM A576 , ASTM A682

SAE Equivalents for JIS S45C
SAE J403 , SAE J412 , SAE J414

AISI Equivalents for JIS S45C
AISI 1045, AISI 1046

EN Equivalents for JIS S45C
EN-8 / BS 970 080M40,Thyssen 1191, ASSAB 760

Chemical Composition

C Si Mn P S
0.42–0.48 0.15–0.35 0.6–0.9 0.030 Max 0.035 Max

Heat Treatment
The following temperature ranges are applicable for the respective heat treatment operations.
Full Annealing 800 – 850°C
Normalising 840 – 880°C
Hardening 820 – 860°C
Quenching medium Water or Oil
Tempering 550 – 660°C

Melting Point
Melting point: 1520 Degree Celsius

Applications

Standard punch head, special punch head and thread rolling tool requiring high precision, long service and abrasion resistance. Various machining tools, e. G. Lathe bit, milling cutter, drill bit, screw tap, round saw and other metal machining tools and wood machining tools. Also suitable for manufacture of forming tools, e. G. Cold extrusion head, extrusion die, punch dies of long service life, and plastic molds of high precision and long service life.

For further info Send by email to: sales@beyond-steel.com
Untuk informasi stock dan update harga terbaru
silahkan menghubungi sales team kami

Related Machinery Steel:

Steel Thyssenkrupp 6582

Product: Thyssenkrupp 6582

Kategori: High Tensile Nickel Chrome Steel

Characteristics
It has high hardenability and is capable of giving good properties in large sections. It is relatively free from temper brittleness and retains useful machinability at relatively high hardness.

Equivalent Thyssen 6582
AISI 4340, DIN 34NiCrMo6, ASSAB 705, VCN 150, JIS SMCM 431, Atlas Ultimo 200

Availability
Round bar

Chemical Composition (%)

C Si Mn P S Ni Cr Mo
0.38-0.43 0.20-0.35 0.60-0.80 0.40 Max 0.04 Max 1.65-2.00 0.70-0.90 0.20-0.30

Mechanical Properties

Hardening Temp : 820 – 850 C
Ouenching Medium : Oil
Hardness as Supplied : 220 – 250 BHN,
Sizes Available : 20mm – 300mm

Applications
Automotive crankshafts and rear axle shafts, aircrafts crankshafts, Connecting Rods, Propeller Hubs, Gears, Drive shafts, Landing gear parts and heavy duty parts of rock drill

Product Machinery Steel:

Harga Steel S45C

Characteristic
Steel S45C is a medium strength steel. Suitable for shafts studs, keys etc. Available as rolled or normalised. Supplied as square bar, or round bar or flat. They are excelling in weldability & machinability , and they can be subjected to various heat treatments. Based on JIS G 4051-2009
Steel S45C Standard and Grade: JIS S45C DIN1.1151 is typical for flame hardening, and can produce a surface hardness of 500 BHN to a depth of 0.10 in this applies particularly to shafts and gears

Availability
Round bar, Flat

Size

Round Bar: Φ 3.2 – 400mm

Flat: 10 – 90 mm & 205 – 305mm or

S45C Mechanical Properties
* Density (kg/m3) 7700-8030
* Young’s Modulus (GPa) 190-210
* Tensile Strength (Mpa) 569 (Standard) 686 (Quenching, Tempering)
* Yield Strength (Mpa) 343 (Standard) 490 (Quenching, Tempering)
* Poisson’s ratio 0.27-0.30

S45C Hardness
Brinell Hardness (HB) 160-220 (Annealed)

S45C Equivalents
DIN Equivalents for JIS S45C
C45, CK45, CF45, CQ45

ASTM Equivalents for JIS S45C
ASTM A29 , ASTM A510 , ASTM A519 , ASTM A576 , ASTM A682

SAE Equivalents for JIS S45C
SAE J403 , SAE J412 , SAE J414

AISI Equivalents for JIS S45C
AISI 1045, AISI 1046

EN Equivalents for JIS S45C
EN-8 / BS 970 080M40,Thyssen 1191, ASSAB 760

S45C Chemical Composition

C Si Mn P S
0.42–0.48 0.15–0.35 0.6–0.9 0.030 Max 0.035 Max

Heat Treatment
The following temperature ranges are applicable for the respective heat treatment operations.
Full Annealing 800 – 850°C
Normalising 840 – 880°C
Hardening 820 – 860°C
Quenching medium Water or Oil
Tempering 550 – 660°C

Melting Point
Melting point: 1520 Degree Celsius

Applications

Standard punch head, special punch head and thread rolling tool requiring high precision, long service and abrasion resistance. Various machining tools, e. G. Lathe bit, milling cutter, drill bit, screw tap, round saw and other metal machining tools and wood machining tools. Also suitable for manufacture of forming tools, e. G. Cold extrusion head, extrusion die, punch dies of long service life, and plastic molds of high precision and long service life.

For further info Send by email to:  sales@beyond-steel.com
Untuk informasi stock dan update harga terbaru
silahkan menghubungi sales team kami

Related Machinery Steel:

Plat Kapal

Characteristic

JIS 3101 SS-400, known as SS400, in the ASME Code Section II-A & JIS specifications of steel plates for general structure included in the category of SA-36. In JIS (Japanese Industrial Standard) “SS” stands for structural steel and 400 grade which is similar to AISI 1018. SS400 is one of the most commonly used hot rolled general structural steel. Typical carbon steel materials, they are very cheap, excelling in weldability & machinability and they can be subjected to various heat treatments.
Availability
Supplied as plates, sheets, flats, bars, sections, etc.
Plate Thickness: 4.5 mm, 6 mm, 8 mm, 10 mm dan 12 mm
Size: 5′ x 20′ , 6′ x 20′ , 4′ x 8′

Mechanical Properties

  • Density (kg/m3): 7860
  • Young’s Modulus (GPa): 190-210
  • Tensile Strength (MPa): 400 – 510 MPa
  • Yield Strength (MPa): 205-245 MPa
  • Poisson’s ratio: 0.26

Hardness
Brinell Hardness (HB) 160

Equivalents
DIN Equivalents for JIS SS400: 17100 St 44-2
ASTM Equivalents for JIS SS400: ASTM A36, ASTM A283 Grade D
EN Equivalents for JIS SS400: EN S275/ BS 43A
Chemical Composition
As per JIS G 3101, Carbon (C), Silicon (Si) and Manganese (Mn) content are not controlled. Phosphorus (P) 0.05% Max and Sulphur (S) 0.05% Max have to controlled below these levels.
Melting Point
Melting point of SS400 is 1430 Degree Celsius
Table Ukuran dan Berat Nominal dan Harga Plat Besi:
Thick
 (mm) WxL (feet)  Weight  Price Rp
1.2 mm x 4×8 28 Kg
1.35 mm x 4×8 31.5 Kg
1.4 mm x 4×8 33 Kg
1.5 mm x 4×8 35 Kg
1.6 mm x 4×8 37.5 Kg
1.8 mm x 4×8 42 Kg
1.9 mm x 4×8 45 Kg
2 mm x 4×8 46.7 Kg
2.1 mm x 4×8 49 Kg
2.3 mm x 4×8 54 Kg
2.5 mm x 4×8 58.3 Kg
2.6 mm x 4×8 60.7 Kg
2.8 mm x 4×8 65.3 Kg
2.9 mm x 4×8 67.7 Kg
3 mm x 4×8 70 Kg
3.2 mm x 4×8 74.7 Kg
3.6 mm x 4×8 84 Kg
3.8 mm x 4×8 88.7 Kg
4 mm x 4×8 93.32 Kg
4.5 mm x 4×8 105 Kg
4.8 mm x 4×8 112 Kg
5 mm x 4×8 117 Kg
5.8 mm x 4×8 135.32 Kg
6 mm x 4×8 140 Kg
8 mm x 4×8 187 Kg
9 mm x 4×8 210 Kg
10 mm x 4×8 233.3 Kg
11 mm x 4×8 256.62 Kg
12 mm x 4×8 280 Kg
13 mm x 4×8 303.3 Kg
14 mm x 4×8 326.62 Kg
15 mm x 4×8 350 Kg
16 mm x 4×8 373 Kg
18 mm x 4×8 420 Kg
19 mm x 4×8 443.3 Kg
20 mm x 4×8 467 Kg
21 mm x 4×8 490 Kg
22 mm x 4×8 513.3 Kg
24 mm x 4×8 560 Kg
25 mm x 4×8 583.3 Kg
28 mm x 4×8 653.24 Kg
30 mm x 4×8 700 Kg
31 mm x 4×8 723.3 Kg
32 mm x 4×8 747 Kg
38 mm x 4×8 887 Kg
40 mm x 4×8 933.2 Kg
42 mm x 4×8 980 Kg
45 mm x 4×8 1050 Kg
50 mm x 4×8 1167 Kg
65 mm x 4×8 1516.5 Kg
75 mm x 4×8 1750 Kg
80 mm x 4×8 1870 Kg
85 mm x 4×8 1983.1 Kg
90 mm x 4×8 2100 Kg
100 mm x 4×8 2333 Kg

Associated Swedish Steels AB Grades

Grades

Cold Work Steel  ASP 23
Cold Work Steel  ASP 30
Cold Work Steel  ASP 60
Cold Work Steel   88
Cold Work Steel   XW-10
Cold Work Steel   XW-41
Cold Work Steel   XW-42
Cold Work Steel   XW-5
Cold Work Steel  CARMO
Cold Work Steel  DF-3
Cold Work Steel  VANADIS 10
Cold Work Steel  VANADIS 4
Cold Work Steel  VANADIS 4

Hot Work Steel material  8407 2M
Hot Work Steel material  8407 SUPREME
Hot Work Steel material  DIEVAR
Hot Work Steel material  HOTVAR
Hot Work Steel material  QRO 90

Machinery Steel  grade 705/ 705M
Machinery Steel  grade 707
Machinery Steel  grade 709/ 709M
Machinery Steel  grade 7210M
Machinery Steel  grade 760

Plastic Mould Steel material  S136 Grade:DIN:1.4034/GB4Cr13
Plastic Mould Steel material  618
Plastic Mould Steel material  718HH
Plastic Mould Steel material  CALMAX
Plastic Mould Steel material  CORRAX
Plastic Mould Steel material  ELMAX
Plastic Mould Steel material  EM33
Plastic Mould Steel material  EM38
Plastic Mould Steel material  MOLDMAX LH/MM
Plastic Mould Steel material  MOLDMAX XL
Plastic Mould Steel material  Polmax
Plastic Mould Steel material  PRODAX
Plastic Mould Steel material  PROTHERM
Plastic Mould Steel material  RAMAX 2
Plastic Mould Steel material  STAVAX ESR
Plastic Mould Steel material  STAVAX Supreme