Harga Plat SM490 YA

Harga Plat SM490 YA

Kategori: Welded Structural Steel Plates
Material: SM490
Standard: JIS G3106
Grades: SM490 YA, SM490 YB

Characteristic:
Steel grade SM490 is a low carbon, high strength for weld structural steel. Easy for weld and good cold forming properties.

Availability:
Thickness: 6 – 60 mm
Size: 5′ x 20′ , 1524 x 6096mm

Chemical Composition: (%)

C Si Mn P S
0.18 Max 0.55 Max 1.60 Max 0.035 Max 0.035 Max

Note: other alloy elements may be added as necessary (Ni, Cr and Cu)

Equivalent Steel Grade
S 355 JR, AE 355 B, E 36-2, Fe 510 B, SS21,32,01, IS 961, A633 Gr.A,C,D, 50 B

Mechanical Properties:
Yield Strength      t≦16    (Min Mpa) :  365
Yield Strength 16≦t≦25 (Min Mpa) :  325-355
Tensile Strength (Mpa)      :   490-610
Elongation t≦16          (Min %) :   15
Elongation 16≦t≦25 (Min %)  :  21

Application:
Machinery parts, mobile equipment, crane, boom, chassis, buildings, bridges and most structural activities.

Lebih Detail »

 

Iklan

Harga Baja VCN

Steel VCN 150

Characteristics
It has high hardenability and is capable of giving good properties in large sections. It is relatively free from temper brittleness and retains useful machinability at relatively high hardness.

Equivalent VCN 150

Thyssen 6582, DIN 34NiCrMo6, ASSAB 705, JIS SMCM 431, AISI 4340

Availability
Round bar

Chemical Composition (%)

C Si Mn P S Ni Cr Mo
0.38–0.43 0.20–0.35 0.60–0.80 0.40 Max 0.040 Max 1.65–2.00 0.70–0.90 0.20-0.30

Mechanical Properties
Hardening Temp : 820 – 850 C
Ouenching Medium : Oil
Hardness as Supplied : 220 – 250 BHN,
Sizes Available : 20mm – 300mm

Applications
Automotive crankshafts and rear axle shafts, aircrafts crankshafts, Connecting Rods, Propeller Hubs, Gears, Drive shafts, Landing gear parts and heavy duty parts of rock drill

Lebih Detail »

Related Machinery Steel:

Harga AISI 1045 Steel

AISI 1045 Steel Roundbar

Characteristic
AISI 1045 Steel is a medium strength steel. Suitable for shafts studs, keys etc. Available as rolled or normalised. Supplied as square bar, or round bar or flat. They are excelling in weldability & machinability , and they can be subjected to various heat treatments. Based on JIS G 4051-2009
AISI 1045 Steel Standard and Grade: JIS S45C DIN1.1151 is typical for flame hardening, and can produce a surface hardness of 500 BHN to a depth of 0.10 in this applies particularly to shafts and gears

Availability
Round bar, Flat

Size

Round Bar: Φ 3.2 – 400mm

Flat: 10 – 90 mm & 205 – 305mm or

Mechanical Properties
* Density (kg/m3) 7700-8030
* Young’s Modulus (GPa) 190-210
* Tensile Strength (Mpa) 569 (Standard) 686 (Quenching, Tempering)
* Yield Strength (Mpa) 343 (Standard) 490 (Quenching, Tempering)
* Poisson’s ratio 0.27-0.30

Hardness
Brinell Hardness (HB) 160-220 (Annealed)

Equivalents
DIN Equivalents for JIS S45C
C45, CK45, CF45, CQ45

ASTM Equivalents for JIS S45C
ASTM A29 , ASTM A510 , ASTM A519 , ASTM A576 , ASTM A682

SAE Equivalents for JIS S45C
SAE J403 , SAE J412 , SAE J414

AISI Equivalents for JIS S45C
AISI 1045, AISI 1046

EN Equivalents for JIS S45C
EN-8 / BS 970 080M40,Thyssen 1191, ASSAB 760

Chemical Composition

C Si Mn P S
0.42–0.48 0.15–0.35 0.6–0.9 0.030 Max 0.035 Max

Heat Treatment
The following temperature ranges are applicable for the respective heat treatment operations.
Full Annealing 800 – 850°C
Normalising 840 – 880°C
Hardening 820 – 860°C
Quenching medium Water or Oil
Tempering 550 – 660°C

Melting Point
Melting point: 1520 Degree Celsius

Applications

Standard punch head, special punch head and thread rolling tool requiring high precision, long service and abrasion resistance. Various machining tools, e. G. Lathe bit, milling cutter, drill bit, screw tap, round saw and other metal machining tools and wood machining tools. Also suitable for manufacture of forming tools, e. G. Cold extrusion head, extrusion die, punch dies of long service life, and plastic molds of high precision and long service life.

For further info Send by email to: sales@beyond-steel.com
Untuk informasi stock dan update harga terbaru
silahkan menghubungi sales team kami

Related Machinery Steel:

Steel 6582

Product: Thyssenkrupp 6582

Kategori: High Tensile Nickel Chrome Steel

Characteristics
It has high hardenability and is capable of giving good properties in large sections. It is relatively free from temper brittleness and retains useful machinability at relatively high hardness.

Equivalent Thyssen 6582
AISI 4340, DIN 34NiCrMo6, ASSAB 705, VCN 150, JIS SMCM 431, Atlas Ultimo 200

Availability
Round bar

Chemical Composition (%)

C Si Mn P S Ni Cr Mo
0.38-0.43 0.20-0.35 0.60-0.80 0.40 Max 0.04 Max 1.65-2.00 0.70-0.90 0.20-0.30

Mechanical Properties

Hardening Temp : 820 – 850 C
Ouenching Medium : Oil
Hardness as Supplied : 220 – 250 BHN,
Sizes Available : 20mm – 300mm

Applications
Automotive crankshafts and rear axle shafts, aircrafts crankshafts, Connecting Rods, Propeller Hubs, Gears, Drive shafts, Landing gear parts and heavy duty parts of rock drill

Product Machinery Steel:

Harga Steel S45C

Characteristic
Steel S45C is a medium strength steel. Suitable for shafts studs, keys etc. Available as rolled or normalised. Supplied as square bar, or round bar or flat. They are excelling in weldability & machinability , and they can be subjected to various heat treatments. Based on JIS G 4051-2009
Steel S45C Standard and Grade: JIS S45C DIN1.1151 is typical for flame hardening, and can produce a surface hardness of 500 BHN to a depth of 0.10 in this applies particularly to shafts and gears

Availability
Round bar, Flat

Size

Round Bar: Φ 3.2 – 400mm

Flat: 10 – 90 mm & 205 – 305mm or

S45C Mechanical Properties
* Density (kg/m3) 7700-8030
* Young’s Modulus (GPa) 190-210
* Tensile Strength (Mpa) 569 (Standard) 686 (Quenching, Tempering)
* Yield Strength (Mpa) 343 (Standard) 490 (Quenching, Tempering)
* Poisson’s ratio 0.27-0.30

S45C Hardness
Brinell Hardness (HB) 160-220 (Annealed)

S45C Equivalents
DIN Equivalents for JIS S45C
C45, CK45, CF45, CQ45

ASTM Equivalents for JIS S45C
ASTM A29 , ASTM A510 , ASTM A519 , ASTM A576 , ASTM A682

SAE Equivalents for JIS S45C
SAE J403 , SAE J412 , SAE J414

AISI Equivalents for JIS S45C
AISI 1045, AISI 1046

EN Equivalents for JIS S45C
EN-8 / BS 970 080M40,Thyssen 1191, ASSAB 760

S45C Chemical Composition

C Si Mn P S
0.42–0.48 0.15–0.35 0.6–0.9 0.030 Max 0.035 Max

Heat Treatment
The following temperature ranges are applicable for the respective heat treatment operations.
Full Annealing 800 – 850°C
Normalising 840 – 880°C
Hardening 820 – 860°C
Quenching medium Water or Oil
Tempering 550 – 660°C

Melting Point
Melting point: 1520 Degree Celsius

Applications

Standard punch head, special punch head and thread rolling tool requiring high precision, long service and abrasion resistance. Various machining tools, e. G. Lathe bit, milling cutter, drill bit, screw tap, round saw and other metal machining tools and wood machining tools. Also suitable for manufacture of forming tools, e. G. Cold extrusion head, extrusion die, punch dies of long service life, and plastic molds of high precision and long service life.

For further info Send by email to:  sales@beyond-steel.com
Untuk informasi stock dan update harga terbaru
silahkan menghubungi sales team kami

Related Machinery Steel:

RI Masih Impor Baja dan Aluminium

Dok News – Detik

Inilah akibatnya jika negara seperti Indonesia yang kaya akan Sumber Daya Alam (SDA) melimpah tetapi tidak bisa mengolahnya, akibatnya untuk membangun kapal, jembatan sampai jalan bahan besinya harus diimpor semua.

Seperti diungkapkan Meteri Perindustrian Mohammad S. Hidayat. Dia mengatakan untuk membangun dermaga, kapal laut, landasan airport, jembatan, rel kereta api, jaringan listrik, telomunikasi dan lain-lain membutuhkan mineral logam seperti besi beton, aluminium, nikel, tembaga dan lainnya tetapi semuanya itu harus diimpor dari luar negeri.

“Untuk membangun itu, kita masih mengandalkan impor bahkan ada yang 100% harus impor, padahal negara yang memproduksi baja, aluminium, nikel dan lainnya ,mendapat pasokan bahan baku dari Indonesia seperti Jepang dan China,” kata Hidayat di kantornya, Jalan Jend. Gatot Subroto.

Seperti Besi Baja, lanjut Hidayat, kebutuhan besi baja dalam negeri saat ini sebanyak 4 juta ton per tahun berupa iron ore, sponge iron, pellet dan skrap dimana seluruhnya masih impor.

“Nikel, industri hilir berbasis nikel seperti stainless steel dan nickel alloy belum tumbuh di dalam negeri. Sementara itu, kebutuhan stainless steel dan nickel alloy untuk memenuhi kebutuhan sektor konstruksi, minyak dan gas, otomotif, elektronik, permesinan, railway, dan lain-lain sangat besar dan sepenuhnya masih diimpor. Nilai tambah produk hilir berbasis nikel akan meningkat 105 kali dibandingkan ekspor bijih nikel,” jelasnya.

Apalagi saat ini terjadi ekspor besar- besaran seperti Aluminium. Pada tahun 2011, ekspor komoditas ini mencapai 40 juta ton per tahun atau naik 5 kali lipat dibanding 2008.

“Dalam beberapa tahun terakhir ekspor besar-besaran juga terjadi pada bijih nikel yaitu sebesar 33 juta ton pada 2011 atau meningkat 8 kali dibandingkan pada 2008,” ucapnya.

Makanya, pemerintah mengeluarkan aturan pengendalian ekspor khususnya pada 2014 tidak boleh lagi bahan mentah yang diekspor dan saat ini untuk 65 jenis bahan mineral jika ingin diekspor mentah-mentah dikenakan bea keluar yang rata-rata sebesar 20%.

“Tujuannya untuk mengendalikan ekspor yang cenderung meningkat drastis. jangan sampai kalau dibiarkan seperti candangan bauksit yang bisa habis 4-5 tahun ke depan, seperti cadangan cadangan terbukti bijih besi bisa habis 9 tahun lagi apabila semuanya tidak dikendalikan ekspornya,” jelasnya.

Sambil menunggu aturan larangan ekspor tersebut yang berlaku pada 2014, pemerintah saat ini terus mendorong investasi di sektor hilir untuk industri pengolahan yakni pabrik smelter besi cor.

“Kita dorong ini, seperti di sektor agrobisnis industri smelternya sudah tumbuh, ini yang kita inginkan juga untuk disektor pertambangan mineral,” tandasnya.

Harga Besi H-beam Standar SNI

Beyond-steel Indonesia menjual baja konstruksi H-Beam berbagai jenis dan ukuran. Untuk Ukuran yang ready stock, maupun informasi pemesanan silahkan mengisi form inquiry yang telah tersedia atau dapat menghubungi sales kami

 

Characteristic

Hot-rolled steel beam with H-shaped cross section, used mainly in piling and retaining structures. A structural beam of rolled steel or concrete having a shape whose cross section resembles the letter H; has wider flanges than an I-beam.

Tabel Ukuran, Berat Nominal & Harga H-Beam » Klik Disini «

Mechanical Properties

Grade

Tensile Test

Impact Test

Thickness

Yield Strength

Tensile Strength

Thickness

Elongation

Temp

V-notch Impact Energy

(mm)

σs (MPa)

σb (MPa)

δ5 (mm)

δ5 (%)

(°C)

Akv (J)

Q235A

≤16

≥235

375-500

≤16

≥26

Q235B

>16-40

≥225

>16-40

≥25

20

≥27

Q235C

>40-60

≥215

>40-60

≥24

0

Q235D

-20

Q345A

≤16

≥345

470-630

≥21

Q345B

>16-40

≥325

20

≥34

Q345C

>40-60

≥295

≥22

0

Q345D

-20

Q345E

-40

≥27

Q345T

≥345

470-630

≥21

20

≥49.54J/cm2 (Akv )

-40

≥23.2J/cm2 (Akv )

SS400

≤16

≥245

400-510

>5-16

≥17

>16-40

≥325

>16-50

≥21

SM400B

≤16

≥245

400-510

>5-16

≥18

0

≥27

>16-40

≥325

>16-50

≥22

SM490B

≤16

≥325

490-610

>5-16

≥17

0

≥27

>16-40

≥315

>16-50

≥21

SM490YB

≤16

≥325

490-610

>5-16

≥15

≥27

>16-75

≥355

>16-50

≥19

ASTM A36

≥250

490-550

200mm

≥20

[36]

[58-80]

ASTM A572(GR50)

≥345

≥450

200mm

≥18

[50]

[65]

ASTM A992

≥345

≥450

200mm

≥18

[50-65]

[65]

ASTM A36/A572 (GR50)/A992

≥345

450-550

200mm

≥21

[50-65]

[65-80]

43A

≤16

≥275

430-580

≥22

>16-40

≥265

50B

≤16

≥355

490-640

≥20

20

≥27

>16-40

≥345

55C

≤16

≥450

550-700

200mm

≥17

0

≥27

>16-25

≥430

>25-40

≥415