Harga Baja VCN

Steel VCN 150

Characteristics
It has high hardenability and is capable of giving good properties in large sections. It is relatively free from temper brittleness and retains useful machinability at relatively high hardness.

Equivalent VCN 150

Thyssen 6582, DIN 34NiCrMo6, ASSAB 705, JIS SMCM 431, AISI 4340

Availability
Round bar

Chemical Composition (%)

C Si Mn P S Ni Cr Mo
0.38–0.43 0.20–0.35 0.60–0.80 0.40 Max 0.040 Max 1.65–2.00 0.70–0.90 0.20-0.30

Mechanical Properties
Hardening Temp : 820 – 850 C
Ouenching Medium : Oil
Hardness as Supplied : 220 – 250 BHN,
Sizes Available : 20mm – 300mm

Applications
Automotive crankshafts and rear axle shafts, aircrafts crankshafts, Connecting Rods, Propeller Hubs, Gears, Drive shafts, Landing gear parts and heavy duty parts of rock drill

Lebih Detail »

Related Machinery Steel:

Iklan

Harga Plat Mild Steel ASTM A-36

Characteristic

Mild Steel Plate, also known as Hot Rolled A36 Steel Plate is a structural quality steel plate used for a large variety of general construction and industrial applications. Mild Steel Plate ASTM A-36 is one of the most commonly used hot rolled general structural steel. Typical carbon steel materials, they are very cheap, excelling in weldability & machinability and they can be subjected to various heat treatments.

Availability
Supplied as plates, sheets, flats, bars, sections, etc.
Plate Thickness: 4.5 mm, 6 mm, 8 mm, 10 mm dan 12 mm
Size: 5′ x 20′ , 6′ x 20′ , 4′ x 8′
Size: Thickness x Width x Length

Specifications
Grade: ASTM A36, AISI A-36
Workability: Easy to Weld, Cut, Form and Machine

Mechanical Properties

  • Density (kg/m3): 7860
  • Young’s Modulus (GPa): 190-210
  • Tensile Strength (MPa): 400 – 510 MPa
  • Yield Strength (MPa): 205-245 MPa
  • Poisson’s ratio: 0.26
  • Brinell Hardness (HB) 160

Equivalents
DIN Equivalents for JIS SS400: 17100 St 44-2
ASTM Equivalents for JIS SS400: ASTM A36, ASTM A283 Grade D
EN Equivalents for JIS SS400: EN S275/ BS 43A

Chemical Composition (%)
Carbon (C), Silicon (Si) and Manganese (Mn) content are not controlled. Phosphorus (P) 0.05% Max and Sulphur (S) 0.05% Max have to controlled below these levels.

Tabel Ukuran & Berat Nominal Plat ASTM A-36:
Product Thickness (mm) Standard Sheet Size Weight per square metre
Mild Steel Plate 3mm 3.00 1200 x 2400mm (1.2 x 2.4m) 23.55
Mild Steel Plate 4mm 4.00 1200 x 2400mm (1.2 x 2.4m) 31.4
Mild Steel Plate 5mm 5.00 1200 x 2400mm (1.2 x 2.4m) 39.25
Mild Steel Plate 6mm 6.00 1200 x 2400mm (1.2 x 2.4m) 47.1
Mild Steel Plate 8mm 8.00 1200 x 2400mm (1.2 x 2.4m) 62.8
Mild Steel Plate 10mm 10.00 1200 x 2400mm (1.2 x 2.4m) 78.5
Mild Steel Plate 12mm 12.00 1200 x 2400mm (1.2 x 2.4m) 94.2
Mild Steel Plate 16mm 16.00 1200 x 2400mm (1.2 x 2.4m) 125.6
Mild Steel Plate 20mm 20.00 1200 x 2400mm (1.2 x 2.4m) 157
Mild Steel Plate 25mm 25.00 1200 x 2400mm (1.2 x 2.4m) 196.25
Melting Point
Melting point of SS400 is 1430 Degree Celsius
Applications:
base plates, gussets, liners, road plates, trench covers, etc.

Related Carbon Steel:

Harga AISI 1045 Steel

AISI 1045 Steel Roundbar

Characteristic
AISI 1045 Steel is a medium strength steel. Suitable for shafts studs, keys etc. Available as rolled or normalised. Supplied as square bar, or round bar or flat. They are excelling in weldability & machinability , and they can be subjected to various heat treatments. Based on JIS G 4051-2009
AISI 1045 Steel Standard and Grade: JIS S45C DIN1.1151 is typical for flame hardening, and can produce a surface hardness of 500 BHN to a depth of 0.10 in this applies particularly to shafts and gears

Availability
Round bar, Flat

Size

Round Bar: Φ 3.2 – 400mm

Flat: 10 – 90 mm & 205 – 305mm or

Mechanical Properties
* Density (kg/m3) 7700-8030
* Young’s Modulus (GPa) 190-210
* Tensile Strength (Mpa) 569 (Standard) 686 (Quenching, Tempering)
* Yield Strength (Mpa) 343 (Standard) 490 (Quenching, Tempering)
* Poisson’s ratio 0.27-0.30

Hardness
Brinell Hardness (HB) 160-220 (Annealed)

Equivalents
DIN Equivalents for JIS S45C
C45, CK45, CF45, CQ45

ASTM Equivalents for JIS S45C
ASTM A29 , ASTM A510 , ASTM A519 , ASTM A576 , ASTM A682

SAE Equivalents for JIS S45C
SAE J403 , SAE J412 , SAE J414

AISI Equivalents for JIS S45C
AISI 1045, AISI 1046

EN Equivalents for JIS S45C
EN-8 / BS 970 080M40,Thyssen 1191, ASSAB 760

Chemical Composition

C Si Mn P S
0.42–0.48 0.15–0.35 0.6–0.9 0.030 Max 0.035 Max

Heat Treatment
The following temperature ranges are applicable for the respective heat treatment operations.
Full Annealing 800 – 850°C
Normalising 840 – 880°C
Hardening 820 – 860°C
Quenching medium Water or Oil
Tempering 550 – 660°C

Melting Point
Melting point: 1520 Degree Celsius

Applications

Standard punch head, special punch head and thread rolling tool requiring high precision, long service and abrasion resistance. Various machining tools, e. G. Lathe bit, milling cutter, drill bit, screw tap, round saw and other metal machining tools and wood machining tools. Also suitable for manufacture of forming tools, e. G. Cold extrusion head, extrusion die, punch dies of long service life, and plastic molds of high precision and long service life.

For further info Send by email to: sales@beyond-steel.com
Untuk informasi stock dan update harga terbaru
silahkan menghubungi sales team kami

Related Machinery Steel:

DC53 Cold Work Die Steels

Description
DC53 is a general purpose cold work tool steel with exceptional Toughness, Wear Resistance, Compressive Strength and Temper Resistance.

Features
Uniform distribution of fine carbides
Excellent galling & wear resistance
Exceptional toughness & fatigue resistance
High temper resistance to support PVD & nitride surface treatments
Machining & grinding characteristics superior to most other tool steels

These properties are obtained through its chemistry as well as its unique manufacturing processes of ladle refinement, vacuum degassing and forging methods. DC53 also has excellent machining characteristics and is well suited as a sub-straight for PVD surface treatments. DC53 can also be hot process CVD and TD (Thermal Diffusion) coated however post heat treat is generally recommended.

Availability
Rounds 1/4″ to 20″
Flats 1/2″ to 12″ thick in widths up to 24″

Chemical Composition (%)

C Si Mn Cr Mo V
0.95 1.00 0.40 8.00 2.00 0.30

Mechanical Properties

Annealed Hardness (BHN): 210 – 225
Specific Gravity (g/Cm3): 7.76
Density (lb/Inch3) : ,2793
Young’s Modulus (E) : 21,700
Modulus of Rigidity (G) : 8,480
Poisson’s Ratio : 0.28

Fabrication Characteristics

Machining

DC53 can typically be machined 20% to 40% faster than D2 while experiencing as much as 50% less tool wear and breakdown.

Faster feeds and speeds reduce machining cost and yielding an improved surface finish.

Wire EDM

DC53 was initially developed with the Wire EDM process in mind. The high temperature double draw 520° C (970° F) or higher was part of the development criteria in determining alloy content, and heat treat requirements for DC53. This high temperature double temper relives a considerable amount of stress in the steel which in turn minimizes movement in the part when Wire EDM cutting hardened DC53. Click here for more information.

Welding

With special care DC53 can be welded. Use any appropriate weld rod such as an H72A rod which is commonly used for high carbon, high chrome die steels similar to D2. The weld rod should be dry to prevent bubble cracks in the weld. Placing the rod in a 350 degrees Celsius (650 degrees Fahrenheit) oven for one hour is generally sufficient.

Applications
Punches & dies, Draw & forum dies, Shear blades, Shredder knives, Thread & form rolls, Cold heading dies, Mill rolls & slitters

Product  Tool Steel:

Harga Steel S45C

Characteristic
Steel S45C is a medium strength steel. Suitable for shafts studs, keys etc. Available as rolled or normalised. Supplied as square bar, or round bar or flat. They are excelling in weldability & machinability , and they can be subjected to various heat treatments. Based on JIS G 4051-2009
Steel S45C Standard and Grade: JIS S45C DIN1.1151 is typical for flame hardening, and can produce a surface hardness of 500 BHN to a depth of 0.10 in this applies particularly to shafts and gears

Availability
Round bar, Flat

Size

Round Bar: Φ 3.2 – 400mm

Flat: 10 – 90 mm & 205 – 305mm or

S45C Mechanical Properties
* Density (kg/m3) 7700-8030
* Young’s Modulus (GPa) 190-210
* Tensile Strength (Mpa) 569 (Standard) 686 (Quenching, Tempering)
* Yield Strength (Mpa) 343 (Standard) 490 (Quenching, Tempering)
* Poisson’s ratio 0.27-0.30

S45C Hardness
Brinell Hardness (HB) 160-220 (Annealed)

S45C Equivalents
DIN Equivalents for JIS S45C
C45, CK45, CF45, CQ45

ASTM Equivalents for JIS S45C
ASTM A29 , ASTM A510 , ASTM A519 , ASTM A576 , ASTM A682

SAE Equivalents for JIS S45C
SAE J403 , SAE J412 , SAE J414

AISI Equivalents for JIS S45C
AISI 1045, AISI 1046

EN Equivalents for JIS S45C
EN-8 / BS 970 080M40,Thyssen 1191, ASSAB 760

S45C Chemical Composition

C Si Mn P S
0.42–0.48 0.15–0.35 0.6–0.9 0.030 Max 0.035 Max

Heat Treatment
The following temperature ranges are applicable for the respective heat treatment operations.
Full Annealing 800 – 850°C
Normalising 840 – 880°C
Hardening 820 – 860°C
Quenching medium Water or Oil
Tempering 550 – 660°C

Melting Point
Melting point: 1520 Degree Celsius

Applications

Standard punch head, special punch head and thread rolling tool requiring high precision, long service and abrasion resistance. Various machining tools, e. G. Lathe bit, milling cutter, drill bit, screw tap, round saw and other metal machining tools and wood machining tools. Also suitable for manufacture of forming tools, e. G. Cold extrusion head, extrusion die, punch dies of long service life, and plastic molds of high precision and long service life.

For further info Send by email to:  sales@beyond-steel.com
Untuk informasi stock dan update harga terbaru
silahkan menghubungi sales team kami

Related Machinery Steel:

Plat Boiler ASTM A-516 Gr.70

Characteristic

The ASTM A 516 carbon steel is widely used in various pressure applications of many industries.

Beyond-steel Indonesia provide steel plates in ASTM A 516 standard that includes carbon steel plates. Our range is primarily used in welded pressure vessels where improved notch toughness is required. The steel plates allow four different strength levels and the most common is grade 70. This grade is made to a fine grain particle size to meet the requirement of varied industry applications. Our steel plates are HIC tested.

Features:

Uniform surface
High tensile strength
Corrosion resistance
Sturdy construction
Temperature resistance

Tabel Ukuran, Berat Nominal dan Harga Plat ASTM A 516 Gr.70

Size Plate Weight (Kg)  Price
3/16″ x 5′ x 20′ = 347 Kg
1/4″ x 5′ x 20′ = 463 Kg
5/16″ x 5′ x 20′ = 579 Kg
3/8″ x 5′ x 20′ = 694 Kg
7/16″ x 5′ x 20′ = 810 Kg
1/2″ x 5′ x 20′ = 926 Kg
9/16″ x 5′ x 20′ = 1042 Kg
5/8″ x 5′ x 20′ = 1158 Kg
3/4″ x 5′ x 20′ = 1389 Kg
1′ x 5′ x 20′ = 1852 Kg

Untuk informasi stock dan update harga terbaru
silahkan menghubungi sales team kami

Related Carbon Steel:

Besi CNP SNI

Deskripsi
Besi Kanal C atau sering juga disebut: CNP, balok purlin, C-channel, profil C biasa digunakan untuk : purlin (balok dudukan penutup atap), girts (elemen yang memegang penutup dinding seperti metal sheet) member pada truss, rangka komponen arsitektural,dll

Tabel Ukuran dan Berat Besi Kanal C (CNP) SNI:
Product Size Berat 
Kanal C 60 X 30 X 10 X 1.6 = 9.8 Kg
Kanal C 60 X 30 X 10 X 2.3 = 13.5 Kg
Kanal C 75 X 35 X 15 X 1.5 = 12 Kg
Kanal C 75 X 45 X 15 X 1.6 = 14 Kg
Kanal C 75 X 45 X 15 X 2.3 = 19.5 Kg
Kanal C 75 X 45 X 20 X 2.3 = 19.5 Kg
Kanal C 100 X 50 X 20 X 1,6 = 24.36 Kg
Kanal C 100 X 50 X 20 X 2.3 = 24.36 Kg
Kanal C 100 X 50 X 20 X 3.2 = 33 Kg
Kanal C 125 X 50 X 20 X 2.3 = 27.06 Kg
Kanal C 125 X 50 X 20 X 3.2 = 37 Kg
Kanal C 150 X 50 X 20 X 2.3 = 30 Kg
Kanal C 150 X 50 X 20 X 3.2 = 40.6 Kg
Kanal C 150 X 65 X 20 X 2.3 = 33 Kg
Kanal C 150 X 65 X 20 X 3.2 = 45.06 Kg
Kanal C 200 X 75 X 20 X 3.2 = 55.62 Kg
Lebih Detail »