Jual Quend 700

Description
Quend 700 is extra high strength structural steel produced as quenched and tempered with a minimum yield strength of 700 MPa. Quend 700 complies with the requirements corresponding to the S690QL given in the EN 10025-6 standard, where impact toughness is guaranteed at -40 °C.

Availability
Quend 700 is currently supplied in the following range:
• thickness: 8 – 25 mm
• width: 1500 – 3000 mm

Chemical Composition (%)

C Si Mn Cr Mo P Ni S B Nb V Ti Al N
 0.20 0.60 1.50 0.60 0.50 0.020 1.00 0.010 0.005 0.040 0.070 0.040 0.070 0.014

Mechanical Properties
Hardness (HBW) : 370 – 430
Charpy-V notch : 35 J
impact test (longitudinal at -40 °C)
Yield Strength (MPa): 700 Min
Tensile Strength (MPa): 780 – 930
Elongation (%): 14

Cutting
Quend 700 may be cut either by oxygen fuel, plasma and laser cutting without any restrictions

Welding
Welding of Quend 700 can be performed using any of the conventional welding methods available both as manual or automatic.

Application
Quend 700 is recommended for the following applications:
• truck chassis
• lifting and hoisting equipment
• handling equipment
• trailers

Related Carbon Steel:

Iklan

Harga Baja VCN

Steel VCN 150

Characteristics
It has high hardenability and is capable of giving good properties in large sections. It is relatively free from temper brittleness and retains useful machinability at relatively high hardness.

Equivalent VCN 150

Thyssen 6582, DIN 34NiCrMo6, ASSAB 705, JIS SMCM 431, AISI 4340

Availability
Round bar

Chemical Composition (%)

C Si Mn P S Ni Cr Mo
0.38–0.43 0.20–0.35 0.60–0.80 0.40 Max 0.040 Max 1.65–2.00 0.70–0.90 0.20-0.30

Mechanical Properties
Hardening Temp : 820 – 850 C
Ouenching Medium : Oil
Hardness as Supplied : 220 – 250 BHN,
Sizes Available : 20mm – 300mm

Applications
Automotive crankshafts and rear axle shafts, aircrafts crankshafts, Connecting Rods, Propeller Hubs, Gears, Drive shafts, Landing gear parts and heavy duty parts of rock drill

Lebih Detail »

Related Machinery Steel:

Harga AISI 1045 Steel

AISI 1045 Steel Roundbar

Characteristic
AISI 1045 Steel is a medium strength steel. Suitable for shafts studs, keys etc. Available as rolled or normalised. Supplied as square bar, or round bar or flat. They are excelling in weldability & machinability , and they can be subjected to various heat treatments. Based on JIS G 4051-2009
AISI 1045 Steel Standard and Grade: JIS S45C DIN1.1151 is typical for flame hardening, and can produce a surface hardness of 500 BHN to a depth of 0.10 in this applies particularly to shafts and gears

Availability
Round bar, Flat

Size

Round Bar: Φ 3.2 – 400mm

Flat: 10 – 90 mm & 205 – 305mm or

Mechanical Properties
* Density (kg/m3) 7700-8030
* Young’s Modulus (GPa) 190-210
* Tensile Strength (Mpa) 569 (Standard) 686 (Quenching, Tempering)
* Yield Strength (Mpa) 343 (Standard) 490 (Quenching, Tempering)
* Poisson’s ratio 0.27-0.30

Hardness
Brinell Hardness (HB) 160-220 (Annealed)

Equivalents
DIN Equivalents for JIS S45C
C45, CK45, CF45, CQ45

ASTM Equivalents for JIS S45C
ASTM A29 , ASTM A510 , ASTM A519 , ASTM A576 , ASTM A682

SAE Equivalents for JIS S45C
SAE J403 , SAE J412 , SAE J414

AISI Equivalents for JIS S45C
AISI 1045, AISI 1046

EN Equivalents for JIS S45C
EN-8 / BS 970 080M40,Thyssen 1191, ASSAB 760

Chemical Composition

C Si Mn P S
0.42–0.48 0.15–0.35 0.6–0.9 0.030 Max 0.035 Max

Heat Treatment
The following temperature ranges are applicable for the respective heat treatment operations.
Full Annealing 800 – 850°C
Normalising 840 – 880°C
Hardening 820 – 860°C
Quenching medium Water or Oil
Tempering 550 – 660°C

Melting Point
Melting point: 1520 Degree Celsius

Applications

Standard punch head, special punch head and thread rolling tool requiring high precision, long service and abrasion resistance. Various machining tools, e. G. Lathe bit, milling cutter, drill bit, screw tap, round saw and other metal machining tools and wood machining tools. Also suitable for manufacture of forming tools, e. G. Cold extrusion head, extrusion die, punch dies of long service life, and plastic molds of high precision and long service life.

For further info Send by email to: sales@beyond-steel.com
Untuk informasi stock dan update harga terbaru
silahkan menghubungi sales team kami

Related Machinery Steel:

Steel 6582

Product: Thyssenkrupp 6582

Kategori: High Tensile Nickel Chrome Steel

Characteristics
It has high hardenability and is capable of giving good properties in large sections. It is relatively free from temper brittleness and retains useful machinability at relatively high hardness.

Equivalent Thyssen 6582
AISI 4340, DIN 34NiCrMo6, ASSAB 705, VCN 150, JIS SMCM 431, Atlas Ultimo 200

Availability
Round bar

Chemical Composition (%)

C Si Mn P S Ni Cr Mo
0.38-0.43 0.20-0.35 0.60-0.80 0.40 Max 0.04 Max 1.65-2.00 0.70-0.90 0.20-0.30

Mechanical Properties

Hardening Temp : 820 – 850 C
Ouenching Medium : Oil
Hardness as Supplied : 220 – 250 BHN,
Sizes Available : 20mm – 300mm

Applications
Automotive crankshafts and rear axle shafts, aircrafts crankshafts, Connecting Rods, Propeller Hubs, Gears, Drive shafts, Landing gear parts and heavy duty parts of rock drill

Product Machinery Steel:

SKD 61 Steel Price

Product  : SKD 61
Standard: JIS
Grade     : Hot Work Tool Steel

High temperature wear resistance and ductility, good heat conductivity, low susceptibility to hot cracks, Good Creep resistance.
In order to bring out its excellent characteristics, SKD61 needs quenching, and after quenching, it is tempered to stabilize the metallographic texture and to improve its toughness. However, since it is known that depending on the conditions of tempering SKD61 causes change of dimensions and reduction of hardness, unforeseen failures can result if the tempering is done without understanding this trend. Therefore, in this course, the tempering characteristics of SKD61 are explained below.

 

Equivalent SKD 61
Thyssen 2344, DIN X40CrMoV51, AISI H13, JIS SKD 61, BOHLER W302 SUPERIOR®

Availability
Roundbar : Ø 10 mm – 303 mm
Square : 10 mm – 100 mm
Plate/Flat Thk : 10 -100 mm
Width : 25-1000 mm
Supplied Condition: Annealed

Harga: Rp. 95.000 – Rp.135.000/ Kg

Chemical composition SKD 61: ( % )

C Si Mn Cr Mo V
0.35-0.40 0.80-1.20 0.25-0.40 4.80-5.50 1.25-1.50 0.85-1.15
Hardening Temp : 820 – 850 C
Ouenching Medium : Oil
Hardness as Supplied

Application SKD 61
Extrusion mandrel, press and forging dies, moulds for pressure casting low density metals, ejector pins, Universal hot work tool steel,etc

Hubungi Kami

Harga Steel S45C

Characteristic
Steel S45C is a medium strength steel. Suitable for shafts studs, keys etc. Available as rolled or normalised. Supplied as square bar, or round bar or flat. They are excelling in weldability & machinability , and they can be subjected to various heat treatments. Based on JIS G 4051-2009
Steel S45C Standard and Grade: JIS S45C DIN1.1151 is typical for flame hardening, and can produce a surface hardness of 500 BHN to a depth of 0.10 in this applies particularly to shafts and gears

Availability
Round bar, Flat

Size

Round Bar: Φ 3.2 – 400mm

Flat: 10 – 90 mm & 205 – 305mm or

S45C Mechanical Properties
* Density (kg/m3) 7700-8030
* Young’s Modulus (GPa) 190-210
* Tensile Strength (Mpa) 569 (Standard) 686 (Quenching, Tempering)
* Yield Strength (Mpa) 343 (Standard) 490 (Quenching, Tempering)
* Poisson’s ratio 0.27-0.30

S45C Hardness
Brinell Hardness (HB) 160-220 (Annealed)

S45C Equivalents
DIN Equivalents for JIS S45C
C45, CK45, CF45, CQ45

ASTM Equivalents for JIS S45C
ASTM A29 , ASTM A510 , ASTM A519 , ASTM A576 , ASTM A682

SAE Equivalents for JIS S45C
SAE J403 , SAE J412 , SAE J414

AISI Equivalents for JIS S45C
AISI 1045, AISI 1046

EN Equivalents for JIS S45C
EN-8 / BS 970 080M40,Thyssen 1191, ASSAB 760

S45C Chemical Composition

C Si Mn P S
0.42–0.48 0.15–0.35 0.6–0.9 0.030 Max 0.035 Max

Heat Treatment
The following temperature ranges are applicable for the respective heat treatment operations.
Full Annealing 800 – 850°C
Normalising 840 – 880°C
Hardening 820 – 860°C
Quenching medium Water or Oil
Tempering 550 – 660°C

Melting Point
Melting point: 1520 Degree Celsius

Applications

Standard punch head, special punch head and thread rolling tool requiring high precision, long service and abrasion resistance. Various machining tools, e. G. Lathe bit, milling cutter, drill bit, screw tap, round saw and other metal machining tools and wood machining tools. Also suitable for manufacture of forming tools, e. G. Cold extrusion head, extrusion die, punch dies of long service life, and plastic molds of high precision and long service life.

For further info Send by email to:  sales@beyond-steel.com
Untuk informasi stock dan update harga terbaru
silahkan menghubungi sales team kami

Related Machinery Steel:

Associated Swedish Steels AB Grades

Grades

Cold Work Steel  ASP 23
Cold Work Steel  ASP 30
Cold Work Steel  ASP 60
Cold Work Steel   88
Cold Work Steel   XW-10
Cold Work Steel   XW-41
Cold Work Steel   XW-42
Cold Work Steel   XW-5
Cold Work Steel  CARMO
Cold Work Steel  DF-3
Cold Work Steel  VANADIS 10
Cold Work Steel  VANADIS 4
Cold Work Steel  VANADIS 4

Hot Work Steel material  8407 2M
Hot Work Steel material  8407 SUPREME
Hot Work Steel material  DIEVAR
Hot Work Steel material  HOTVAR
Hot Work Steel material  QRO 90

Machinery Steel  grade 705/ 705M
Machinery Steel  grade 707
Machinery Steel  grade 709/ 709M
Machinery Steel  grade 7210M
Machinery Steel  grade 760

Plastic Mould Steel material  S136 Grade:DIN:1.4034/GB4Cr13
Plastic Mould Steel material  618
Plastic Mould Steel material  718HH
Plastic Mould Steel material  CALMAX
Plastic Mould Steel material  CORRAX
Plastic Mould Steel material  ELMAX
Plastic Mould Steel material  EM33
Plastic Mould Steel material  EM38
Plastic Mould Steel material  MOLDMAX LH/MM
Plastic Mould Steel material  MOLDMAX XL
Plastic Mould Steel material  Polmax
Plastic Mould Steel material  PRODAX
Plastic Mould Steel material  PROTHERM
Plastic Mould Steel material  RAMAX 2
Plastic Mould Steel material  STAVAX ESR
Plastic Mould Steel material  STAVAX Supreme