Harga Baja VCN

Steel VCN 150

Characteristics
It has high hardenability and is capable of giving good properties in large sections. It is relatively free from temper brittleness and retains useful machinability at relatively high hardness.

Equivalent VCN 150

Thyssen 6582, DIN 34NiCrMo6, ASSAB 705, JIS SMCM 431, AISI 4340

Availability
Round bar

Chemical Composition (%)

C Si Mn P S Ni Cr Mo
0.38–0.43 0.20–0.35 0.60–0.80 0.40 Max 0.040 Max 1.65–2.00 0.70–0.90 0.20-0.30

Mechanical Properties
Hardening Temp : 820 – 850 C
Ouenching Medium : Oil
Hardness as Supplied : 220 – 250 BHN,
Sizes Available : 20mm – 300mm

Applications
Automotive crankshafts and rear axle shafts, aircrafts crankshafts, Connecting Rods, Propeller Hubs, Gears, Drive shafts, Landing gear parts and heavy duty parts of rock drill

Lebih Detail »

Related Machinery Steel:

Iklan

Harga Plat Mild Steel ASTM A-36

Characteristic

Mild Steel Plate, also known as Hot Rolled A36 Steel Plate is a structural quality steel plate used for a large variety of general construction and industrial applications. Mild Steel Plate ASTM A-36 is one of the most commonly used hot rolled general structural steel. Typical carbon steel materials, they are very cheap, excelling in weldability & machinability and they can be subjected to various heat treatments.

Availability
Supplied as plates, sheets, flats, bars, sections, etc.
Plate Thickness: 4.5 mm, 6 mm, 8 mm, 10 mm dan 12 mm
Size: 5′ x 20′ , 6′ x 20′ , 4′ x 8′
Size: Thickness x Width x Length

Specifications
Grade: ASTM A36, AISI A-36
Workability: Easy to Weld, Cut, Form and Machine

Mechanical Properties

  • Density (kg/m3): 7860
  • Young’s Modulus (GPa): 190-210
  • Tensile Strength (MPa): 400 – 510 MPa
  • Yield Strength (MPa): 205-245 MPa
  • Poisson’s ratio: 0.26
  • Brinell Hardness (HB) 160

Equivalents
DIN Equivalents for JIS SS400: 17100 St 44-2
ASTM Equivalents for JIS SS400: ASTM A36, ASTM A283 Grade D
EN Equivalents for JIS SS400: EN S275/ BS 43A

Chemical Composition (%)
Carbon (C), Silicon (Si) and Manganese (Mn) content are not controlled. Phosphorus (P) 0.05% Max and Sulphur (S) 0.05% Max have to controlled below these levels.

Tabel Ukuran & Berat Nominal Plat ASTM A-36:
Product Thickness (mm) Standard Sheet Size Weight per square metre
Mild Steel Plate 3mm 3.00 1200 x 2400mm (1.2 x 2.4m) 23.55
Mild Steel Plate 4mm 4.00 1200 x 2400mm (1.2 x 2.4m) 31.4
Mild Steel Plate 5mm 5.00 1200 x 2400mm (1.2 x 2.4m) 39.25
Mild Steel Plate 6mm 6.00 1200 x 2400mm (1.2 x 2.4m) 47.1
Mild Steel Plate 8mm 8.00 1200 x 2400mm (1.2 x 2.4m) 62.8
Mild Steel Plate 10mm 10.00 1200 x 2400mm (1.2 x 2.4m) 78.5
Mild Steel Plate 12mm 12.00 1200 x 2400mm (1.2 x 2.4m) 94.2
Mild Steel Plate 16mm 16.00 1200 x 2400mm (1.2 x 2.4m) 125.6
Mild Steel Plate 20mm 20.00 1200 x 2400mm (1.2 x 2.4m) 157
Mild Steel Plate 25mm 25.00 1200 x 2400mm (1.2 x 2.4m) 196.25
Melting Point
Melting point of SS400 is 1430 Degree Celsius
Applications:
base plates, gussets, liners, road plates, trench covers, etc.

Related Carbon Steel:

Harga AISI 1045 Steel

AISI 1045 Steel Roundbar

Characteristic
AISI 1045 Steel is a medium strength steel. Suitable for shafts studs, keys etc. Available as rolled or normalised. Supplied as square bar, or round bar or flat. They are excelling in weldability & machinability , and they can be subjected to various heat treatments. Based on JIS G 4051-2009
AISI 1045 Steel Standard and Grade: JIS S45C DIN1.1151 is typical for flame hardening, and can produce a surface hardness of 500 BHN to a depth of 0.10 in this applies particularly to shafts and gears

Availability
Round bar, Flat

Size

Round Bar: Φ 3.2 – 400mm

Flat: 10 – 90 mm & 205 – 305mm or

Mechanical Properties
* Density (kg/m3) 7700-8030
* Young’s Modulus (GPa) 190-210
* Tensile Strength (Mpa) 569 (Standard) 686 (Quenching, Tempering)
* Yield Strength (Mpa) 343 (Standard) 490 (Quenching, Tempering)
* Poisson’s ratio 0.27-0.30

Hardness
Brinell Hardness (HB) 160-220 (Annealed)

Equivalents
DIN Equivalents for JIS S45C
C45, CK45, CF45, CQ45

ASTM Equivalents for JIS S45C
ASTM A29 , ASTM A510 , ASTM A519 , ASTM A576 , ASTM A682

SAE Equivalents for JIS S45C
SAE J403 , SAE J412 , SAE J414

AISI Equivalents for JIS S45C
AISI 1045, AISI 1046

EN Equivalents for JIS S45C
EN-8 / BS 970 080M40,Thyssen 1191, ASSAB 760

Chemical Composition

C Si Mn P S
0.42–0.48 0.15–0.35 0.6–0.9 0.030 Max 0.035 Max

Heat Treatment
The following temperature ranges are applicable for the respective heat treatment operations.
Full Annealing 800 – 850°C
Normalising 840 – 880°C
Hardening 820 – 860°C
Quenching medium Water or Oil
Tempering 550 – 660°C

Melting Point
Melting point: 1520 Degree Celsius

Applications

Standard punch head, special punch head and thread rolling tool requiring high precision, long service and abrasion resistance. Various machining tools, e. G. Lathe bit, milling cutter, drill bit, screw tap, round saw and other metal machining tools and wood machining tools. Also suitable for manufacture of forming tools, e. G. Cold extrusion head, extrusion die, punch dies of long service life, and plastic molds of high precision and long service life.

For further info Send by email to: sales@beyond-steel.com
Untuk informasi stock dan update harga terbaru
silahkan menghubungi sales team kami

Related Machinery Steel:

Stainless Steel 316 Sheet&Roundbar

Dear valued customers,

Beyond-Steel menjual Stainless Steel 316 acerinox, Jindal, Heisei, Outokumpu import plat, sheet, roundbar dan chanel dengan ukuran dan ketebalan bervariasi. Untuk informasi stock dan harga silahkan hubungi kami:

Tel  : Contact
Fax : Contact
Mobile: Contact
E-mail: sales@beyond-steel.com

Grades 316

Stainless steel grades 316 and 316L are also known as types 1.4401 and 1.4404 respectively. Grade 316 is an austenitic grade second only to 304 in commercial importance. 316 stainless steel contains an addition of molybdenum that gives it improved corrosion resistance. This is particularly apparent for pitting and crevice corrosion in chloride environments. 316L, the low carbon version of 316 stainless steel, is immune to grain boundary carbide precipitation (sensitisation). This makes it suited to use in heavy gauge (over about 6mm) welded components.

For elevated temperature applications the high carbon variant, 316H stainless steel and the stabilised grade 316Ti stainless steel should be employed. The austenitic structure of 316 stainless steel gives excellent toughness, even at cryogenic temperatures.

Property data given in this document is typical for flat rolled products covered by ASTM A240/A240M. ASTM, EN or other standards may cover products. It is reasonable to expect specifications in these standards to be similar but not necessarily identical to those given in this datasheet.

Availability
Stainless steel 316 is available in Sheet, Bar, Wire, Rod, Strip, tube, pipe, and Channel.
Stainless steel SUS 316 Sheet
Stainless steel SUS 316 Plate
Stainless steel SUS 316 Rod
Stainless steel SUS 316 Tube
Stainless steel SUS 316 Pipe
Stainless steel SUS 316 Channel

Tecnical Data Stainless steel 316 Beyond-steel Indonesia

Chemical Composition (%)

C : 0.05 – 0.08
Si : <= 1.00
Mn : <= 2.00
Ni : 10.00 – 14.00
Cr : 16.00 – 18.00
Mo : 2.00 – 3.00

Mechanical Properties
Tensile Strength : 53 Kgf/MM2
Yield Strength (0.2%) : >= 21 Kgf/MM2
Elongation (%) : >= 40%
Hardness : <= 187 HB

Corrosion Resistance

SUS 316 grade has excellent corrosion resistance when exposed to a range of corrosive environments and media. It is usually regarded as “marine grade” stainless steel but is not resistant to warm sea water. Warm chloride environments can cause pitting and crevice corrosion. Grade 316 is also subject to stress corrosion cracking above around 60°C.

Heat Resistance
SUS316 has good resistance to oxidation in intermittent service to 870°C and in continuous service to 925°C. However, continuous use at 425-860°C is not recommended if corrosion resistance in water is required. In this instance 316L is recommended due to its resistance to carbide precipitation. Where high strength is required at temperatures above 500°C, grade 316H is recommended.

Fabrication

Fabrication of all stainless steels should be done only with tools dedicated to stainless steel materials. Tooling and work surfaces must be thoroughly cleaned before use. These precautions are necessary to avoid cross contamination of stainless steel by easily corroded metals that may discolour the surface of the fabricated product.

Cold Working

Grade 316 is readily brake or roll formed into a variety of parts. It is also suited to stamping, heading and drawing but post work annealing is recommended to relieve internal stresses. Cold working will increase both strength and hardness of 316 stainless steel.

Hot Working

All common hot working processes can be performed on 316 stainless steel. Hot working should be avoided below 927°C. The ideal temperature range for hot working is 1149-1260°C. Post-work annealing is recommended to ensure optimum corrosion resistance.

Heat Treatment
316 stainless steel cannot be hardened by heat treatment. Solution treatment or annealing can be done by rapid cooling after heating to 1010-1120°C.

Machinability
316 stainless steel has good machinability. Machining can be enhanced using the following rules:

  • Cutting edges must be kept sharp. Dull edges cause excess work hardening.
  • Cuts should be light but deep enough to prevent work hardening by riding on the surface of the material.
  • Chip breakers should be employed to assist in ensuring swarf remains clear of the work
  • Low thermal conductivity of austenitic alloys results in heat concentrating at the cutting edges. This means coolants and lubricants are necessary and must be used in large quantities.
Welding
Fusion welding performance for 316 stainless steel is excellent both with and without fillers. Recommended filler rods and electrodes for 316 and 316L are the same as the base metal, 316 and 316L respectively. Heavy welded sections may require post-weld annealing. Grade 316Ti may be used as an alternative to 316 in heavy section welds. Oxyacetylene welding has not been found to be successful for joining of 316 stainless steel.
Stainless Steel 316Ti
Another variation of 316 is available. This variation is 316Ti. Stainless steel grade 316Ti contains a small amount of titanium. Titanium content is typically only around 0.5%. The titanium atoms stabilise the structure of the 316 at temperatures over 800°C. This prevents carbide precipitation at the grain boundaries and protects the metal from corrosion. The main advantage of 316Ti is that it can be held at higher temperatures for a longer period without sensitisation Linkprecipitation) occurring. 316Ti retains physical and mechanical properties similar to standard grades of 316.

Plat Stainless steel 316 4’x8′ Weight table

Stainless Steel Size Berat (Kg)
Plate 316 1 mm x 4′ x 8′ 23.6 Kg
Plate 316 2 mm x 4′ x 8′ 47.2 Kg
Plate 316 3 mm x 4′ x 8′ 70.8 Kg
Plate 316 4 mm x 4′ x 8′ 94.4 Kg
Plate 316 5 mm x 4′ x 8′ 118 Kg
Plate 316 6 mm x 4′ x 8′ 141.6 Kg
Plate 316 8 mm x 4′ x 8′ 188.8 Kg
Plate 316 10 mm x 4′ x 8′ 236 Kg
Plate 316 12mm x 4′ x 8′ 283.2 Kg
Untuk berat stainless steel 316 dengan ketebalan diatas 12mm (>12mm) silahkan menghubungi sales team kami di: sales@beyond-steel.com

Applications

316 Stainless Steel is now typically used in:

  • Food processing equipment
  • Chemical and petrochemical equipment
  • Laboratory benches & equipment
  • Coastal architectural panelling
  • Coastal balustrading
  • Boat fittings
  • Chemical transportation containers
  • Heat exchangers
  • Mining screens
  • Nuts and bolts
  • Springs
  • Medical implants

Beyond-steel Indonesia, distributor 316 stainless steel indonesia jual 316 stainless steel, jual plat 316 stainless steel, jual 316 stainless steel sheet, jual 316 stainless steel batangan, jual 316 stainless steel round bar, jual 316 stainless steel plate, jual 316 stainless steel wire,ukuran 316 stainless steel,harga 316 stainless steel,diameter 316 stainless steel, plat 316 stainless steel,beli 316 stainless steel,distributor 316 stainless steel,tebal 316 stainless steel,berat 316 stainless steel,pabrik 316 stainless steel, stockist 316 stainless steel,grade 316 stainless steel, suplier 316 stainless steel,chemical composition 316 stainless steel, equivalent of 316 stainless steel, mechanical properties 316 stainless steel, physical properties 316 stainless steel, properties of 316 stainless steel, hrc 316 stainless steel,thickness 316 stainless steel, hardness 316 stainless steel melayani pengiriman seluruh indonesia

Related Stainless Steel:

Harga Plat Deemex

Dear valued customers,
Beyond-Steel menjual plat DEEMEX Grade DMX 100, DMX 105, DMX 110 import, dengan ukuran dan ketebalan bervariasi. Untuk informasi stock dan harga silahkan hubungi kami:
Tel  : +62-021-3293 5972
Fax : +62-021-8837 6742
Mobile: +62-0858 8044 6226
E-mail: sales@beyond-steel.com

Characteristic

DEEMEX Plates reduce maintenance and operating costs providing longer service life. The production line is suited in Greece (EU).We assure quality by analyzing the microstructure and chemical composition in every batch. All the production is fully automated and all raw materials are checked for purity and test certificates.

The finished product is checked for composition, carbide content, tolerances, crack dimension and straightness from fully equipped testing lab.

We deliver DEEMEX Plates with all certificates DIN 50049-2.2 for coating and EN 10204:2004-3.1 for base plates, according to EN ISO 9001:2008.

The newest production line of DEEMEX Plates employs PLC controlled systems ensuring uniform coating bead width and various welding shape imprints.
DEEMEX Plates outlast in high abrasion applications quench and tempered steels by up to 9 times and up to 42 times mild steel according to ASTM G65 -00 standard testing.

DEEMEX  SERIES
WEAR PLATES
C.
(%)
Cr.
(%)
OTHER
ELEMENTS
HARDNESS
ROCKWELL
PLATE THICKNESS
PLATE
COATING
DMX 100
2.7-4.3
17-29
Mn, B, Mo, Fe
50-56
≥4mm
≥3mm
≤10mm
DMX 105
4.1-5.1
30-32
Mn, B, Mo, Fe
56-60
≥4mm
≥3mm
≤10mm
DMX 110
4.9-5.5
32-35
Mn, B,  Mo, Fe
60-64
≥4mm
≥3mm
≤12mm
The Wear Plate Series (DMX100, DMX105, DMX110)
comes with Standard Base Material.

Related Wear Plates:

Steel 6582

Product: Thyssenkrupp 6582

Kategori: High Tensile Nickel Chrome Steel

Characteristics
It has high hardenability and is capable of giving good properties in large sections. It is relatively free from temper brittleness and retains useful machinability at relatively high hardness.

Equivalent Thyssen 6582
AISI 4340, DIN 34NiCrMo6, ASSAB 705, VCN 150, JIS SMCM 431, Atlas Ultimo 200

Availability
Round bar

Chemical Composition (%)

C Si Mn P S Ni Cr Mo
0.38-0.43 0.20-0.35 0.60-0.80 0.40 Max 0.04 Max 1.65-2.00 0.70-0.90 0.20-0.30

Mechanical Properties

Hardening Temp : 820 – 850 C
Ouenching Medium : Oil
Hardness as Supplied : 220 – 250 BHN,
Sizes Available : 20mm – 300mm

Applications
Automotive crankshafts and rear axle shafts, aircrafts crankshafts, Connecting Rods, Propeller Hubs, Gears, Drive shafts, Landing gear parts and heavy duty parts of rock drill

Product Machinery Steel:

Harga SKD11 Tool Steel

Product  : SKD 11
Standard: JIS
Grade       : Cold Work Tool Steel

Characteristics SKD 11

SKD11 tool steel grades, trade name SLD (the latest improved version called SLD-MAGIC), the product called DC11 or SLD high wear-resistant chromium cold work tool steel or JIS G4404 (SKD11) / AISI D2

Chemical Composition SKD 11

C Si Mn Cr Mo V P S
1.5 0.25 0.45 12.00 1.00 0.35 0.025 0.01

Hardness
Soft annealing to about HB210 (Soft Annealed Approximately HB210)

Features
Common cold of high wear-resistant tool steel; quenching of the good, less heat deformation.

Advantages:

  • Was vacuum degassing refining, so the quality is very clean inside
  • Machining of good
  • Hardenability, good air cooling can be hardened without fear of quenching crack
  • Heat treatment deformation is very small, very small quenching deviation, the most suitable for precision mold
  • Very good wear resistance, the most suitable for stainless steel or high Die Hard Materials
  • Good toughness.

Application SKD 11
This steel is easy turning, and should be made sharp knife, scissors, saw, cold or hot for repair mode, the drum side, the screw pattern, line mode, cutters, impact mode, circular cylinder, the system of power transformers heart dies, cutting steel Paper mill knives, steel forming rollers, special molding roller, precision rules, shape complexity of the cold tools, mandrels, metallurgy, tin for mold, plastic mold, the screw head molds.

Related Tool Steel: