Tabel Perbandingan Equivalent Stainless

Tabel Perbandingan Material Stainless Steel

Equivalent Standar JIS, GB, ASTM, DIN & ISO

USA
Japan
China
Germany
ISO
ASTMA276-96 JIS G4303-91 GB 1220-92 DIN17400-96 683/13-86
/ AISI DINEN10088-1-95 TR4956/84
201 SUS201 1Cr17Mn6Ni5N X12CrMnNiN 17-7-5 A-2
202 SUS202 1Cr18Mn8Ni5N X12CrMnNiN 18-9-5 A-3
301 SUS301 1Cr17Ni7 14
302 SUS302 1Cr18Ni9 DIN17440-96
X12CrNi18-9
12
303 SUS303 Y1Cr18Ni9 X12CrNiS18-9 17
303Se SUS303Se Y1Cr18Ni9Se 17a
304 SUS304 0Cr18Ni9 X5CrNi18-10 11
304L SUS304L 00Cr19Ni11 X2CrNi19-11 10
304N SUS304N1 0Cr19Ni9N
XM21 SUS304N2 0Cr19Ni10NbN
SUS304LN 00Cr18Ni10N X2CrNiN18-10 10N
305 SUS305 1Cr18Ni12 X4CrNi18-12 13
309S SUS309S 0Cr23Ni13 15
310S SUS310S 0Cr25Ni20 16
316 SUS316 0Cr17Ni12Mo2 X5CrNiMo17-12-2 20/ 20a
316Ti S31635 SUS316Ti 0Cr18Ni12Mo2Ti X6CrNiMoTi17-12-2 21
316L SUS316L 00Cr17Ni14Mo2 X2CrNiMo18-14-3 19
/ 19 a
316N SUS316N 0Cr17Ni12Mo2N X5CrNiMo17-12-2
316LN SUS316LN 00Cr17Ni13Mo2N X2CrNiMoN17-11-2 19N/ 19aN
SUS316J1 0Cr18Ni12Mo2Cu2
SUS316JIL 00Cr18Ni14Mo2Cu2
317 SUS317 0Cr19Ni13Mo3 X5CrNiMo17-13-3
317L SUS317L 00Cr19Ni13Mo3 X2CrNiMo18-15-4 24
SUS317J1 0Cr18Ni16Mo5
321 1Cr18Ni9Ti X6CrNitI18-10 11
321 SUS321 0Cr18Ni10Ti X6CrNiTi18-10 15
347 SUS347 0Cr18Ni11Nb X6CrNiNb18-10 16
XM7 SUSXM7 0Cr18Ni9Cu3 X3CrNiCu18-9-4
XM15 SUSXM15J1 0Cr18Ni13Si4
SUS329J1 0Cr26Ni5Mo2
1Cr18Ni11Si4AlTi
405 SUS405 0Cr13Al X6CrAl13 5
SUS410L 00Cr12
430 SUS430 1Cr17 X6Cr17 8
SUS430F YCr17 X6CrMoS17 8a
SUS434 1Cr17Mo X6CrMo17-1 9c
SUS447J1 00Cr30Mo2
XM27 SUSXM27 00Cr27Mo
403 SUS403 1Cr12 X6Cr13 3
410 SUS410 1Cr13 X12Cr13 3
405 SUS405 0Cr13Ae X6Cr13 1
SUS416 Y1Cr13 7
SUS410J1 1Cr13Mo X12CrM126
420 SUS420J1 2Cr13 X20Cr13 4
420 SUS420J2 3Cr13 X30Cr13 5
SUS420F Y3Cr13
4Cr13 X46Cr13
431 SUS431 1Cr17Ni2 X17CrNi16-2 96
SUS440A 7Cr17
SUS440B 8Cr17
SUS440C 9Cr17
SUS440C 11Cr17
SUS440F Y11Cr17
440C SUS440C 9Cr18Mo
9Cr18MoV X90CrMoV18
17-4PH SUS630 0Cr17Ni4Cu4Nb X5CrNiCuNb 16-4 ISO683/16-76
Zeron 100 X2CrNiMoCuWN25-7-4
Lebih Detail »
Iklan

King Cross Steel

Product: King Cross
Kategori: Structural Steel
Standard: JIS, SNI

Availability
Size range : K 150 x 75 to K 800 x 300
Web Thickness Range : 5mm to 14mm
Flange Thickness Range : 7mm to 26mm
Length Standard : 12M

Note: non standard sizes are also available upon request and subject to minimum quantity.

Tabel Ukuran dan Berat Steel King Cross

Sectional Depth Width Web Flange Corner Sectional Area Unit Weight
H x B H B t1 t2 r
mm mm mm mm mm mm mm2 kg/m
150 x 75 150 75 5 7 8 35.7 28
198 x 99 198 99 4.5 7 11 46.36 36.4
200 x 100 200 100 5.5 8 11 54.32 42.6
248 x 124 248 124 5 8 12 65.36 51.4
250 x 125 250 125 6 9 12 75.32 59.2
298 x 149 298 149 5.5 8 13 81.6 64
300 x 150 300 150 6.5 9 13 93.56 73.4
346 x 174 346 174 6 9 14 105.36 82.8
350 x 175 350 175 7 11 14 126.28 99.2
396 x 199 396 199 7 11 16 144.32 113.2
400 x 200 400 200 8 13 16 168.24 132
450 x 200 450 200 9 14 18 193.52 152
500 x 200 500 200 10 16 20 228.4 179.2
588 x 300 588 300 12 20 28 385 302
600 x 200 600 200 11 17 22 268.8 212
700 x 300 700 300 13 24 28 471 369.7
800 x 300 800 300 14 26 28 534 419.8

NOTE :
– H = H/2 = Height of T-Beam
– Material specification refer to Wide Flange (IWF)
– Tolerance H= ±2mm
– Welded specification as per AWS E-6013
– Non standard sizes are available upon request and subject to minimum quantity

Related Structural Steel:

Harga Plat SM490 YB

Harga Plat SM490 YB

Kategori: Welded Structural Steel Plates
Material: SM490
Standard: JIS G3106
Grades: SM490 YA, SM490 YB

Characteristic:
Steel grade SM490 is a low carbon, high strength for weld structural steel. Easy for weld and good cold forming properties.

Availability:
Thickness: 6 – 60 mm
Size: 5′ x 20′ , 1524 x 6096mm

Chemical Composition: (%)

C Si Mn P S
0.18 Max 0.55 Max 1.60 Max 0.035 Max 0.035 Max

Note: other alloy elements may be added as necessary (Ni, Cr and Cu)

Equivalent Steel Grade
S 355 JR, AE 355 B, E 36-2, Fe 510 B, SS21,32,01, IS 961, A633 Gr.A,C,D, 50 B

Mechanical Properties:
Yield Strength      t≦16    (Min Mpa) :  365
Yield Strength 16≦t≦25 (Min Mpa) :  325-355
Tensile Strength (Mpa)      :   490-610
Elongation t≦16          (Min %) :   15
Elongation 16≦t≦25 (Min %)  :  21

Application:
Machinery parts, mobile equipment, crane, boom, chassis, buildings, bridges and most structural activities.

Lebih Detail »

Jual Plat Bisclad600, Bisclad650 & 700

Description
Bisclad is a chromium carbide clad mild steel plate offering outstanding wear life for areas subject to sliding abrasion wear.

Chemical Composition

Grade C
%
PCM
(IIW)
600 4.2 36
650 3.5 – 4.2 20 – 25
750 4.8 – 5.5 29 – 32

Fabrication

Bisclad can be rolled, bent, weld use low hydrogen 7018 electrode and cut with plasma arc. All cutting should be from the mild steel side, otherwise chromium and carbon will contaminate mild steel base and cause a brittle weld.

Bisclad can be supplied with the following means of attachment:

• Plug weld holes
• Stud welded studs to mild steel
• Countersunk holes

Mechanical Properties

Properties Grade Typical
Hardness 600
650
750
600 BHN (57 HRc)
650 HV
750 HV

Application

• Wear plates for draglines
• Shovel
• Hopper
• Skid Plates
• Chutes
• Deflector
• Slurry Pipes
• Dust Pipes

Product Carbon Steel:

Jual Quend 700

Description
Quend 700 is extra high strength structural steel produced as quenched and tempered with a minimum yield strength of 700 MPa. Quend 700 complies with the requirements corresponding to the S690QL given in the EN 10025-6 standard, where impact toughness is guaranteed at -40 °C.

Availability
Quend 700 is currently supplied in the following range:
• thickness: 8 – 25 mm
• width: 1500 – 3000 mm

Chemical Composition (%)

C Si Mn Cr Mo P Ni S B Nb V Ti Al N
 0.20 0.60 1.50 0.60 0.50 0.020 1.00 0.010 0.005 0.040 0.070 0.040 0.070 0.014

Mechanical Properties
Hardness (HBW) : 370 – 430
Charpy-V notch : 35 J
impact test (longitudinal at -40 °C)
Yield Strength (MPa): 700 Min
Tensile Strength (MPa): 780 – 930
Elongation (%): 14

Cutting
Quend 700 may be cut either by oxygen fuel, plasma and laser cutting without any restrictions

Welding
Welding of Quend 700 can be performed using any of the conventional welding methods available both as manual or automatic.

Application
Quend 700 is recommended for the following applications:
• truck chassis
• lifting and hoisting equipment
• handling equipment
• trailers

Related Carbon Steel:

Jual Quard Abrasion Resistant Steel

Description
Quard is a martesitic abrasion resistant steel, with an average hardness of 370 – 550 HBW. The steel offers very high resistance to abrasive wear and impact granting a longer service life. The combination of very good cold forming properties and excellent weldability makes Quard an optimal choice for most wear applications.

Range 
Quard 400 Viewmore »
Quard 450 Viewmore »
Quard 500 and 550 Viewmore »

Availability
Thickness: 8 – 20 mm
Width: 1500 – 2500 mm
Length: maximum 13 m

Welding
Welding Quard is easy and produces outstanding results.
Quard can be welded using any conventional welding method, both manually and automatically.
Due to the low carbon equivalents of Quard, preheating prior to welding is unnecessary in a thickness up to 20 mm.
On account of the tight thickness and flatness tolerances, Quard is well suited for automatic welding.
Quard can also be welded to any other weldable steel.

Bending

Quard has excellent cold forming properties, promoting new innovative solutions for lightweight design.

The excellent bending performance of Quard is achieved by:

  • low levels of non metallic inclusions
  • consistent mechanical properties
  • high crack resistance
  • tight thickness tolerances
  • excellent surface finish
  • consistent spring back
  • Numerous welding operations can be replaced by bending, resulting in a further reduction of production costs.

Cutting

Thermal or cold cutting methods can be used for Quard steel.
Thermal cutting, using either oxygen fuel, plasma or laser cutting is as easy as cutting mild steel.
Quard does not require preheating prior to thermal cutting.
Cold cutting methods, such as abrasive water jet cutting, shearing or sawing have the advantages of not thermally affecting the part being cut, thus avoiding the softening of small parts being produced.

Machining
Quard can be machined in the same way as for any martensitic wear plates of the same hardness.
For drilling, either HSS (8%Co) or indexable cemented carbide drills can be used.
Face milling and countersinking best takes place using tools with replaceable cemented carbide inserts.
For all machining operations performed on Quard, stable machines should be used in order to keep tool set-up vibrations to a minimum.

Application
Dumper bodies, crushers, impact hammers, buckets, feeders, conveyors, bulldozers, compactors, cutters in shredders, etc.

Product Wear Plates:

Jual Plat Quard 500 and Quard 550

Jual Plat Quard 500 and Quard 550

Description
Quard 500 and Quard 550 are intended for use in harsh applications where very high abrasion resistance is essential.
As these products will be produced in the same high standard of quality, like all other Quard wear plates, they will offer the same advantages such as superior surface quality, perfect flatness and tight thickness tolerances.

Availability
Thickness: 8 – 20 mm
Width: 1500 – 2500 mm
Length: maximum 13 m

Application
Dumper bodies, crushers, impact hammers, buckets, feeders, conveyors, bulldozers,  compactors, cutters in shredders, etc.

Product Wear Plates: