Tabel Perbandingan Equivalent Stainless

Tabel Perbandingan Material Stainless Steel

Equivalent Standar JIS, GB, ASTM, DIN & ISO

ASTMA276-96 JIS G4303-91 GB 1220-92 DIN17400-96 683/13-86
/ AISI DINEN10088-1-95 TR4956/84
201 SUS201 1Cr17Mn6Ni5N X12CrMnNiN 17-7-5 A-2
202 SUS202 1Cr18Mn8Ni5N X12CrMnNiN 18-9-5 A-3
301 SUS301 1Cr17Ni7 14
302 SUS302 1Cr18Ni9 DIN17440-96
303 SUS303 Y1Cr18Ni9 X12CrNiS18-9 17
303Se SUS303Se Y1Cr18Ni9Se 17a
304 SUS304 0Cr18Ni9 X5CrNi18-10 11
304L SUS304L 00Cr19Ni11 X2CrNi19-11 10
304N SUS304N1 0Cr19Ni9N
XM21 SUS304N2 0Cr19Ni10NbN
SUS304LN 00Cr18Ni10N X2CrNiN18-10 10N
305 SUS305 1Cr18Ni12 X4CrNi18-12 13
309S SUS309S 0Cr23Ni13 15
310S SUS310S 0Cr25Ni20 16
316 SUS316 0Cr17Ni12Mo2 X5CrNiMo17-12-2 20/ 20a
316Ti S31635 SUS316Ti 0Cr18Ni12Mo2Ti X6CrNiMoTi17-12-2 21
316L SUS316L 00Cr17Ni14Mo2 X2CrNiMo18-14-3 19
/ 19 a
316N SUS316N 0Cr17Ni12Mo2N X5CrNiMo17-12-2
316LN SUS316LN 00Cr17Ni13Mo2N X2CrNiMoN17-11-2 19N/ 19aN
SUS316J1 0Cr18Ni12Mo2Cu2
SUS316JIL 00Cr18Ni14Mo2Cu2
317 SUS317 0Cr19Ni13Mo3 X5CrNiMo17-13-3
317L SUS317L 00Cr19Ni13Mo3 X2CrNiMo18-15-4 24
SUS317J1 0Cr18Ni16Mo5
321 1Cr18Ni9Ti X6CrNitI18-10 11
321 SUS321 0Cr18Ni10Ti X6CrNiTi18-10 15
347 SUS347 0Cr18Ni11Nb X6CrNiNb18-10 16
XM7 SUSXM7 0Cr18Ni9Cu3 X3CrNiCu18-9-4
XM15 SUSXM15J1 0Cr18Ni13Si4
SUS329J1 0Cr26Ni5Mo2
405 SUS405 0Cr13Al X6CrAl13 5
SUS410L 00Cr12
430 SUS430 1Cr17 X6Cr17 8
SUS430F YCr17 X6CrMoS17 8a
SUS434 1Cr17Mo X6CrMo17-1 9c
SUS447J1 00Cr30Mo2
XM27 SUSXM27 00Cr27Mo
403 SUS403 1Cr12 X6Cr13 3
410 SUS410 1Cr13 X12Cr13 3
405 SUS405 0Cr13Ae X6Cr13 1
SUS416 Y1Cr13 7
SUS410J1 1Cr13Mo X12CrM126
420 SUS420J1 2Cr13 X20Cr13 4
420 SUS420J2 3Cr13 X30Cr13 5
SUS420F Y3Cr13
4Cr13 X46Cr13
431 SUS431 1Cr17Ni2 X17CrNi16-2 96
SUS440A 7Cr17
SUS440B 8Cr17
SUS440C 9Cr17
SUS440C 11Cr17
SUS440F Y11Cr17
440C SUS440C 9Cr18Mo
9Cr18MoV X90CrMoV18
17-4PH SUS630 0Cr17Ni4Cu4Nb X5CrNiCuNb 16-4 ISO683/16-76
Zeron 100 X2CrNiMoCuWN25-7-4
Lebih Detail »

Stainless Steel 310

Product : AISI 310
Kategori: Stainless Steel
Grades : Chromium-Nickel steel
Standard: Austenitic

AISI 310 is an Austenitic Standard grade Stainless Steel. It is commonly called AISI Type 310 Chromium-Nickel steel.

Stainless Steel 310 Technical Data

Chemical Composition: (%)

C Mn Si Cr Ni P S
0.25 2.00 1.50 24.0-26.0 19.0-22.0 0.045 0.03

France: AFNOR Z 12 CNS 25.20
Germany: DIN 1.4841
Italy: UNI X 16 CrNiSi 25 20 , UNI X 22 CrNi 25 20
Japan: JIS SUS 310
United Kingdom: B.S. 310 S 24
United States: AMS 5694 , AMS 5695 , ASME SA182 , ASME SA213 , ASME SA249 , ASME SA312 , ASME SA358 , ASME SA403 , ASME SA409 , ASTM A167 , ASTM A182 , ASTM A213 , ASTM A249 , ASTM A276 , ASTM A312 , ASTM A314 , ASTM A358 , ASTM A403 , ASTM A409 , ASTM A473 , ASTM A511 , ASTM A580 , ASTM A632 , FED QQ-S-763 , FED QQ-S-766 , FED QQ-W-423 , FED STD-66 , MIL SPEC MIL-S-862 , SAE 30310 , SAE J405 (30310) , UNS S31000

Mechanical Properties
Density (×1000 kg/m3) 8
Poisson’s Ratio 0.27-0.30
Elastic Modulus (GPa) 200
Tensile Strength (Mpa) 515
Yield Strength (Mpa) 205
Elongation (%) 40
Reduction in Area (%) 50
Hardness (HRB) 95 (max)

Physical Properties
Thermal Expansion (10-6/ºC) 15.9
Thermal Conductivity (W/m-K) 14.2
Specific Heat (J/kg-K) 500
Electric Resistivity (10-9W-m) 780


  • Sinks and splashbacks
  • Saucepans
  • Cutlery and flatware
  • Architectural panelling
  • Sanitaryware and troughs
  • Tubing
  • Brewery, dairy, food and pharmaceutical production equipment

Product Stainless Steel:

Stainless Steel 304

Dear valued customers,

Beyond-Steel menjual Stainless Steel 304 acerinox,Jindal, Heisei, Outokumpu import plat, sheet, roundbar dan chanel dengan ukuran dan ketebalan bervariasi. Untuk informasi stock dan harga silahkan hubungi kami:

Tel  : +62-021-2986 1684

Fax : +62-021-2986 1684

Mobile: +62-0819 0804 5114


Characteristic Grades 304

Stainless steel grade 304 is the most versatile and widely used stainless steel. It is still sometimes referred to by its old name 18/8 which is derived from the nominal composition of type 304 being 18% chromium and 8% nickel. Stainless steel types 1.4301 and 1.4307 are also known as grades 304 and 304L respectively.

Stainless steel 304 is an austenitic grade that can be severely deep drawn. This property has resulted in 304 being the dominant grade used in applications like sinks and saucepans.

Stainless steel 304L is the low carbon version of 304. It is used in heavy gauge components for improved weldability. Some products such as plate and pipe may be available as “dual certified” material that meets the criteria for both 304 and 304L. 304H, a high carbon content variant, is also available for use at high temperatures.

Property data given in this document is typical for flat rolled products covered by ASTM A240/A240M. ASTM, EN or other standards may cover products sold. It is reasonable to expect specifications in these standards to be similar but not necessarily identical to those given in this datasheet.


Stainless steel 304 is available in Sheet, Bar, Wire, Rod, Strip, tube, pipe, and Channel, For all stock availability contact Sales.

Stainless steel 304 Sheet

Stainless steel 304 Plate

Stainless steel 304 Rod

Stainless steel 304 Tube

Stainless steel 304 Pipe

Stainless steel 304 Channel

Stainless Steel 304 Technical Data

Chemical Composition (%)

C : 0.05 – 0.08

Si : <= 1.0

Mn: <= 2.00

Ni : 8.00 – 11.00

Cr : 18.00 – 20.00

Tensile Strength (0.2%) : >= 53 Kgf/MM2

Yield Strength : >= 21 Kgf/MM2

Elongation : >= 40%

Hardness (HB) : <= 187 HB

Corrosion Resistance

304 has excellent corrosion resistance in a wide variety of environments and when in contact with different corrosive media. Pitting and crevice corrosion can occur in environments containing chlorides. Stress corrosion cracking can occur at temperatures over 60°C.
Heat ResistanceJustify Full304 has good resistance to oxidation in intermittent service up to 870°C and in continuous service to 925°C. However, continuous use at 425-860°C is not recommended if corrosion resistance in water is required. In this instance 304L is recommended due to its resistance to carbide precipitation.Where high strength is required at temperatures above 500°C and up to 800°C, grade 304H is recommended. This material will retain aqueous corrosion resistance.

Fabrication of all stainless steels should be done only with tools dedicated to stainless steel materials. Tooling and work surfaces must be thoroughly cleaned before use.These precautions are necessary to avoid cross contamination of stainless steel by easily corroded metals that may discolour the surface of the fabricated product.

Cold Working

304 stainless steel readily work hardens. Fabrication methods involving cold working may require an intermediate annealing stage to alleviate work hardening and avoid tearing or cracking. At the completion of fabrication a full annealing operation should be employed to reduce internal stresses

Hot Working

Fabrication methods, like forging, that involve hot working should occur after uniform heating to 1149-1260°C. The fabricated components should then be rapidly cooled to ensure maximum corrosion resistance.

Heat Treatment

304 stainless steel cannot be hardened by heat treatment. Solution treatment or annealing can be done by rapid cooling after heating to 1010-1120°C.


304 stainless steel has good machinability. Machining can be enhanced using the following rules:

  • Cutting edges must be kept sharp. Dull edges cause excess work hardening.
  • Cuts should be light but deep enough to prevent work hardening by riding on the surface of the material.
  • Chip breakers should be employed to assist in ensuring swarf remains clear of the work
  • Low thermal conductivity of austenitic alloys results in heat concentrating at the cutting edges. This means coolants and lubricants are necessary and must be used in large quantities.

Fusion welding performance for type 304 stainless steel is excellent both with and without fillers. Recommended filler rods and electrodes for stainless steel 304 is grade 308 stainless steel. For 304L the recommended filler is 308L. Heavy welded sections may require post-weld annealing. This step is not required for 304L. Grade 321 may be used if post-weld heat treatment is not possible.


Tabel Ukuran dan Berat Plat stainless steel 304 4’x8′ Beyond-steel Indonesia:

Stainless Steel Size  Berat (Kg)
Plate 304 1 mm x 4′ x 8′ 23.6 Kg
Plate 304 2 mm x 4′ x 8′ 47.2 Kg
Plate 304 3 mm x 4′ x 8′ 70.8 Kg
Plate 304 4 mm x 4′ x 8′ 94.4 Kg
Plate 304 5 mm x 4′ x 8′ 118 Kg
Plate 304 6 mm x 4′ x 8′ 141.6 Kg
Plate 304 8 mm x 4′ x 8′ 188.8 Kg
Plate 304 10 mm x 4′ x 8′ 236 Kg
Plate 304 12mm x 4′ x 8′ 283.2 Kg


304 stainless steel is typically used in:

  • Sinks and splashbacks
  • Saucepans
  • Cutlery and flatware
  • Architectural panelling
  • Sanitaryware and troughs
  • Tubing
  • Brewery, dairy, food and pharmaceutical production equipment
  • Springs, nuts, bolts and screws
  • Medical implants

Related Stainless Steel: