Tabel Perbandingan Equivalent Stainless

Tabel Perbandingan Material Stainless Steel

Equivalent Standar JIS, GB, ASTM, DIN & ISO

ASTMA276-96 JIS G4303-91 GB 1220-92 DIN17400-96 683/13-86
/ AISI DINEN10088-1-95 TR4956/84
201 SUS201 1Cr17Mn6Ni5N X12CrMnNiN 17-7-5 A-2
202 SUS202 1Cr18Mn8Ni5N X12CrMnNiN 18-9-5 A-3
301 SUS301 1Cr17Ni7 14
302 SUS302 1Cr18Ni9 DIN17440-96
303 SUS303 Y1Cr18Ni9 X12CrNiS18-9 17
303Se SUS303Se Y1Cr18Ni9Se 17a
304 SUS304 0Cr18Ni9 X5CrNi18-10 11
304L SUS304L 00Cr19Ni11 X2CrNi19-11 10
304N SUS304N1 0Cr19Ni9N
XM21 SUS304N2 0Cr19Ni10NbN
SUS304LN 00Cr18Ni10N X2CrNiN18-10 10N
305 SUS305 1Cr18Ni12 X4CrNi18-12 13
309S SUS309S 0Cr23Ni13 15
310S SUS310S 0Cr25Ni20 16
316 SUS316 0Cr17Ni12Mo2 X5CrNiMo17-12-2 20/ 20a
316Ti S31635 SUS316Ti 0Cr18Ni12Mo2Ti X6CrNiMoTi17-12-2 21
316L SUS316L 00Cr17Ni14Mo2 X2CrNiMo18-14-3 19
/ 19 a
316N SUS316N 0Cr17Ni12Mo2N X5CrNiMo17-12-2
316LN SUS316LN 00Cr17Ni13Mo2N X2CrNiMoN17-11-2 19N/ 19aN
SUS316J1 0Cr18Ni12Mo2Cu2
SUS316JIL 00Cr18Ni14Mo2Cu2
317 SUS317 0Cr19Ni13Mo3 X5CrNiMo17-13-3
317L SUS317L 00Cr19Ni13Mo3 X2CrNiMo18-15-4 24
SUS317J1 0Cr18Ni16Mo5
321 1Cr18Ni9Ti X6CrNitI18-10 11
321 SUS321 0Cr18Ni10Ti X6CrNiTi18-10 15
347 SUS347 0Cr18Ni11Nb X6CrNiNb18-10 16
XM7 SUSXM7 0Cr18Ni9Cu3 X3CrNiCu18-9-4
XM15 SUSXM15J1 0Cr18Ni13Si4
SUS329J1 0Cr26Ni5Mo2
405 SUS405 0Cr13Al X6CrAl13 5
SUS410L 00Cr12
430 SUS430 1Cr17 X6Cr17 8
SUS430F YCr17 X6CrMoS17 8a
SUS434 1Cr17Mo X6CrMo17-1 9c
SUS447J1 00Cr30Mo2
XM27 SUSXM27 00Cr27Mo
403 SUS403 1Cr12 X6Cr13 3
410 SUS410 1Cr13 X12Cr13 3
405 SUS405 0Cr13Ae X6Cr13 1
SUS416 Y1Cr13 7
SUS410J1 1Cr13Mo X12CrM126
420 SUS420J1 2Cr13 X20Cr13 4
420 SUS420J2 3Cr13 X30Cr13 5
SUS420F Y3Cr13
4Cr13 X46Cr13
431 SUS431 1Cr17Ni2 X17CrNi16-2 96
SUS440A 7Cr17
SUS440B 8Cr17
SUS440C 9Cr17
SUS440C 11Cr17
SUS440F Y11Cr17
440C SUS440C 9Cr18Mo
9Cr18MoV X90CrMoV18
17-4PH SUS630 0Cr17Ni4Cu4Nb X5CrNiCuNb 16-4 ISO683/16-76
Zeron 100 X2CrNiMoCuWN25-7-4
Lebih Detail »

Stainless Steel 316 Sheet&Roundbar

Dear valued customers,

Beyond-Steel menjual Stainless Steel 316 acerinox, Jindal, Heisei, Outokumpu import plat, sheet, roundbar dan chanel dengan ukuran dan ketebalan bervariasi. Untuk informasi stock dan harga silahkan hubungi kami:

Tel  : Contact
Fax : Contact
Mobile: Contact

Grades 316

Stainless steel grades 316 and 316L are also known as types 1.4401 and 1.4404 respectively. Grade 316 is an austenitic grade second only to 304 in commercial importance. 316 stainless steel contains an addition of molybdenum that gives it improved corrosion resistance. This is particularly apparent for pitting and crevice corrosion in chloride environments. 316L, the low carbon version of 316 stainless steel, is immune to grain boundary carbide precipitation (sensitisation). This makes it suited to use in heavy gauge (over about 6mm) welded components.

For elevated temperature applications the high carbon variant, 316H stainless steel and the stabilised grade 316Ti stainless steel should be employed. The austenitic structure of 316 stainless steel gives excellent toughness, even at cryogenic temperatures.

Property data given in this document is typical for flat rolled products covered by ASTM A240/A240M. ASTM, EN or other standards may cover products. It is reasonable to expect specifications in these standards to be similar but not necessarily identical to those given in this datasheet.

Stainless steel 316 is available in Sheet, Bar, Wire, Rod, Strip, tube, pipe, and Channel.
Stainless steel SUS 316 Sheet
Stainless steel SUS 316 Plate
Stainless steel SUS 316 Rod
Stainless steel SUS 316 Tube
Stainless steel SUS 316 Pipe
Stainless steel SUS 316 Channel

Tecnical Data Stainless steel 316 Beyond-steel Indonesia

Chemical Composition (%)

C : 0.05 – 0.08
Si : <= 1.00
Mn : <= 2.00
Ni : 10.00 – 14.00
Cr : 16.00 – 18.00
Mo : 2.00 – 3.00

Mechanical Properties
Tensile Strength : 53 Kgf/MM2
Yield Strength (0.2%) : >= 21 Kgf/MM2
Elongation (%) : >= 40%
Hardness : <= 187 HB

Corrosion Resistance

SUS 316 grade has excellent corrosion resistance when exposed to a range of corrosive environments and media. It is usually regarded as “marine grade” stainless steel but is not resistant to warm sea water. Warm chloride environments can cause pitting and crevice corrosion. Grade 316 is also subject to stress corrosion cracking above around 60°C.

Heat Resistance
SUS316 has good resistance to oxidation in intermittent service to 870°C and in continuous service to 925°C. However, continuous use at 425-860°C is not recommended if corrosion resistance in water is required. In this instance 316L is recommended due to its resistance to carbide precipitation. Where high strength is required at temperatures above 500°C, grade 316H is recommended.


Fabrication of all stainless steels should be done only with tools dedicated to stainless steel materials. Tooling and work surfaces must be thoroughly cleaned before use. These precautions are necessary to avoid cross contamination of stainless steel by easily corroded metals that may discolour the surface of the fabricated product.

Cold Working

Grade 316 is readily brake or roll formed into a variety of parts. It is also suited to stamping, heading and drawing but post work annealing is recommended to relieve internal stresses. Cold working will increase both strength and hardness of 316 stainless steel.

Hot Working

All common hot working processes can be performed on 316 stainless steel. Hot working should be avoided below 927°C. The ideal temperature range for hot working is 1149-1260°C. Post-work annealing is recommended to ensure optimum corrosion resistance.

Heat Treatment
316 stainless steel cannot be hardened by heat treatment. Solution treatment or annealing can be done by rapid cooling after heating to 1010-1120°C.

316 stainless steel has good machinability. Machining can be enhanced using the following rules:

  • Cutting edges must be kept sharp. Dull edges cause excess work hardening.
  • Cuts should be light but deep enough to prevent work hardening by riding on the surface of the material.
  • Chip breakers should be employed to assist in ensuring swarf remains clear of the work
  • Low thermal conductivity of austenitic alloys results in heat concentrating at the cutting edges. This means coolants and lubricants are necessary and must be used in large quantities.
Fusion welding performance for 316 stainless steel is excellent both with and without fillers. Recommended filler rods and electrodes for 316 and 316L are the same as the base metal, 316 and 316L respectively. Heavy welded sections may require post-weld annealing. Grade 316Ti may be used as an alternative to 316 in heavy section welds. Oxyacetylene welding has not been found to be successful for joining of 316 stainless steel.
Stainless Steel 316Ti
Another variation of 316 is available. This variation is 316Ti. Stainless steel grade 316Ti contains a small amount of titanium. Titanium content is typically only around 0.5%. The titanium atoms stabilise the structure of the 316 at temperatures over 800°C. This prevents carbide precipitation at the grain boundaries and protects the metal from corrosion. The main advantage of 316Ti is that it can be held at higher temperatures for a longer period without sensitisation Linkprecipitation) occurring. 316Ti retains physical and mechanical properties similar to standard grades of 316.

Plat Stainless steel 316 4’x8′ Weight table

Stainless Steel Size Berat (Kg)
Plate 316 1 mm x 4′ x 8′ 23.6 Kg
Plate 316 2 mm x 4′ x 8′ 47.2 Kg
Plate 316 3 mm x 4′ x 8′ 70.8 Kg
Plate 316 4 mm x 4′ x 8′ 94.4 Kg
Plate 316 5 mm x 4′ x 8′ 118 Kg
Plate 316 6 mm x 4′ x 8′ 141.6 Kg
Plate 316 8 mm x 4′ x 8′ 188.8 Kg
Plate 316 10 mm x 4′ x 8′ 236 Kg
Plate 316 12mm x 4′ x 8′ 283.2 Kg
Untuk berat stainless steel 316 dengan ketebalan diatas 12mm (>12mm) silahkan menghubungi sales team kami di:


316 Stainless Steel is now typically used in:

  • Food processing equipment
  • Chemical and petrochemical equipment
  • Laboratory benches & equipment
  • Coastal architectural panelling
  • Coastal balustrading
  • Boat fittings
  • Chemical transportation containers
  • Heat exchangers
  • Mining screens
  • Nuts and bolts
  • Springs
  • Medical implants

Beyond-steel Indonesia, distributor 316 stainless steel indonesia jual 316 stainless steel, jual plat 316 stainless steel, jual 316 stainless steel sheet, jual 316 stainless steel batangan, jual 316 stainless steel round bar, jual 316 stainless steel plate, jual 316 stainless steel wire,ukuran 316 stainless steel,harga 316 stainless steel,diameter 316 stainless steel, plat 316 stainless steel,beli 316 stainless steel,distributor 316 stainless steel,tebal 316 stainless steel,berat 316 stainless steel,pabrik 316 stainless steel, stockist 316 stainless steel,grade 316 stainless steel, suplier 316 stainless steel,chemical composition 316 stainless steel, equivalent of 316 stainless steel, mechanical properties 316 stainless steel, physical properties 316 stainless steel, properties of 316 stainless steel, hrc 316 stainless steel,thickness 316 stainless steel, hardness 316 stainless steel melayani pengiriman seluruh indonesia