Harga Plat Bisalloy 400

Harga Plat Bisalloy 400

Characteristic

Bisalloy400 is a through hardened, abrasion resistant steel plate , offering long life expectancy in high impact abrasion applications.

Chemical Composition (%)

Thickness C P Mn Si S Cr Mo B CE
(IIW)*
CET*
5 – < 16 Maximum 0.18 0.025 1.5 0.25 0.008 0.25 0.25 0.002 0.40 0.29
>= 16 – 80 Maximum 0.20 0.025 1.5 0.25 0.008 0.30 0.25 0.002 0.50 0.35
> 80 – 100 Maximum 0.18 0.025 1.5 0.25 0.008 1.20 0.25 0.002 0.58 0.34

Fabrication

Bisalloy400 is high hardness, abra sion resistant steel offering very good impact toughness properties.

Bisalloy400 provides an optimum combination of abrasion resistant, toughness and weldability. Due to its low alloy content, Bisalloy400 can be readily welded using conventional welding processes and low hydrogen consumables.

Cold forming of Bisalloy400 is achievable on all thicknesses although an allowance for the higher strength should be taken into account. Bending machine capabilities should also be taken into consideration prior to any forming operation. Heating above 250ºC should be avoided, otherwise mechanical properties may be affected.

Mechanical Properties

Properties Specification Typical
0,2% Proof Stress 1070 MPa
Tensile Strength 1320 MPa
Elongation in 50mm G.L 14%
Charpy Impact (longitudinal) +20ºC (10mm x 10mm) 55 J
Hardness 370 – 430 HB 400 HB

Application

Bisalloy400 offers excellent wear and abrasion resistant and impact toughness in applications which include:

• Dump Truck Wear Liners
• Screw Conveyors
• Chutes
• Storage Bins
• Earth Moving Buckets
• Cyclones
• Deflector Plates
• Ground Engaging Tools
• Cutting Edges

Product Wear Plates:

Ympress Plate

Description
Ympress is the brand name for the series of hot-rolled High-Strength Low-Alloy steel produced by TMCP (Thermal Mechanical Control Process). Through customer focus the Ympress range has been continuously improved and widened to match the increasing requirements of our customers. Ympress delivers high strength steel with consistent properties, excellent surface quality and high formability. To ensure an optimum match with standards, all grades have been designed to meet or exceed specifications conform EN 10149.

Ympress offer a wide range of strength levels between S315MC up to S700MC and a broad dimensional range with gauges between 1.5 and 20 mm and widths up to 2070 mm. Because of the wide dimensional range and the number of strength levels included in the Ympress brand, Ympress can be used for many applications ranging from construction profiles to crane booms.

Chemical Composition

C Mn Si P S Altot Nb V Ti Mo
Guaranteed ≤ 0.08 ≤ 1.90 ≤ 0.15 0.003 ≤ 0.05 ≤ 0.015 ≤ 0.09 ≤ 0.01 ≤ 0.15 ≤ 0.02
Typical CEV 0.35
Typical Pcm 0.16 (Japanese welding society standard)

Mechanical Properties

Thickness ReH in MPa Rm in MPa A80 in % Adp5 in %
Typical 2 – 3 mm 825 840 13
4 – 8 mm 800 845 19
8 – 10 mm 750 825 18
Guaranteed ≥ 690 750 – 950 ≥ 12 ≥ 14
Bend 0.5t for thickness ≤ 3mm
1t for thickness ≤ 6mm
1.5t for thickness > 6mm

Ympress Benefits

The consistency in chemical composition and production conditions provide the basis for the consistency in product properties of Ympress. Through its properties Ympress contributes to an optimum and efficient processing and high quality finished products.

  • Formability:
    The precise control of the sulphur content prevents the formation of MnS particles resulting in improved bending characteristics for Ympress. Even the use of a very small bending radius (0t) is possible for many strength levels. The guaranteed elongation levels are leading in the European industry.
  • Consistency:
    Ympress’ consistent properties and narrow gauge control ensure the same bending behaviour from sheet to sheet and from coil to coil. This reduces the intermediate setup times for tooling and increases efficiency.
  • Welding:
    The guaranteed low carbon equivalent allows Ympress to be welded trouble free with the commonly used welding methods. Pre- or post heating of the steel is therefore not necessary.
  • Galvanising:
    Most Ympress can directly be galvanised, the very low silicon content prevents the formation of surface defects by the Sandelin effect. For the highest strength levels E690TM and S700MC it is recommended to test the galvanising conditions first.
  • Laser cutting:
    For the optimisation of your laser cutting process we recommend the use of Ympress Laser. Ympress Laser is a superior product because of the low tensions in the material, the low silicon content and the extra high surface quality.
  • High surface quality:
    The low silicon content of all Ympress grades avoids the formation of so called ‘tiger stripes’ . The high quality surface can lead to fewer processing steps during manufacture.

Fabrication

The low carbon equivalent of Ympress makes it readily weldable and permits the use of high welding speeds. There is no need for pre-or post-welding treatment.

Adjacent to the weld a narrow Heat Affected Zone (HAZ) with a slightly decreased hardness is produced, however, with standard welding techniques this has no practical significance.

Tensile tests taken transverse to the weld show the same tensile strength as the parent material.

Stress relieving should be done in temperature ranges of 980° – 1080° F. Heating above this range reduces strength and should be avoided.

Application

Ympress combines high strength with excellent formability and weldability. It is used in applications such :

• Earth Moving Vehicles
• Large Cranes / Mobile Cranes
• Telescopic Booms

In these applications the high strength of steel is used to save weight and increase the load bearing capacity.

Product Wear Plates:

Creusabro 4800 & 8000

Characteristic

For wear and tear which is not only caused by impact and friction, we provide CREUSABRO 4800 and CREUSABRO 8000. These products have TRIP (Transformation Induced by Plasticity) character and micro carbides that make this product have an active surface resistance, so that this material can last better if there is an impact. This product o can also be used in medium temperature 250–450 C, where other resistance product which generates from water quenched process usually will not be functioning optimally.

Creusabro 4000
The new Creusabro concept-excellent ability to work harden and contribution of micro carbides-gives Creusabro 4000 high wear resistance, on average 4 times higher than ordinary mild steel and 30 % higher than conventional 4000 BHN water quenched steel.

To ease in fabricating, Creusabro 4000 is supplied by approximately 360 HB hardness. After the fabrication, the hardness of Creusabro 4000 can be reach 420 HB.

Chemical Composition:

C : 0.20 max
Mn : 1.40
Cr : 0.85 min
Mo : 0.10 min
Ni : 0.30
S : 0.010 max
P : 0.018 max

Applications:
Mines: Extractors, Unloaders, Spiral Chutes. Crusher, Grinders, Screens, Conveyor
Quarries and Construction Earth Moving: Shovels, Diggers, Graders, Bulldozers, Dumpers, Dredging machines, Crushers, Grinders, Screens, Hoppers, Mixers, Molds for concrete aggregates
Cement Plants, Refractory Products: Crushers, Hoppers, Chutes, Cyclone, Wheel Excavator Buckets Metallurgical Plant, Scrap recovery, etc

The Creusabro concept-excellent ability to work harden and the supplementary contribution of microcarbides, already used in Creusabro 4000 has been improved in the Creusabro 8000. this grade takes advantage of an additional metal working process: the TRIP effect (Transformation Induce by Plasticity). The combination of this properties give to the Creusabro 8000 an exceptional wear resistance in heavy plates with uniform properties throughout the thickness around 8 times that of the standard mild steel (A572 G65 grade). The properties in extreme conditions are 50% superior to standard water quenched steel (hardness 500HB).

Creusabro 8000

Creusabro 8000 is supplied with the hardness of 420 HB in order to easy the fabrication. After fabrication, the hardness of Creusabro 8000 can reach 540 HB.

Chemical Compositions:
C Mn Cr Mo Ni S P
0.280 max 1.60 max 1.60 max 0.20 min 0.40 0.005 max 0.015 max

Applications:

Mines, Coal mines: Extracting and load equipment, Hopper lateral liner plate, Helical gravity conveyor.
Quarries and Construction Earth Moving: Blades, Outside Stiffeners, Under teeth pads of loaders and shovel dippers, Crushers and Mills lateral armor plate, Feed crown-wheel, Sprocket-wheal.
Cement Plants: Liners for drier-tubes, Buckets, Hoppers, Clinker cooler outlet shields.
Iron and Steel Industry: Scrap recovery, Brick works, Agricultural equipment, etc.

beyond-steel indonesia, distributor creusabro indonesia jual creusabro, ukuran creusabro,harga creusabro,diameter creusabro,dia. creusabro,beli creusabro,distributor creusabro,tebal creusabro,berat creusabro,pabrik creusabro, stockist creusabro,grade creusabro, suplier creusabro,chemical composition creusabro, equivalent of creusabro, mechanical properties creusabro, physical properties creusabro, properties of creusabro, hrc creusabro,thickness creusabro, hardness creusabro

Plat FORA 400

Characteristic

FORA 400 is a water quenched maternistic steel, with a typical hardness of 400HB (42,5HRC), constituting a real answer to abrasive wear. Thanks to its toughness, its elevated hardness, its high yield strength, FORA 400 can be use wherever a wear resistance to wear by sliding or by moderate impacts is required. Moreover, FORA 400 is very easily welded and has a good forming properties thereby contributing to ease of fabrication.

Compared to conventional steels, such as S355, FORA 400 offers a real benefit to the equipment life times and permits a signifiant reduction in he design thickness since its wear resistance is up to 3 times longer than S355 grade.

Moreover, FORA 400 is very easily welded and has a good forming properties thereby contributing to ease of fabrication. This steel is particulary suitable for applications in quarries, construction industry, mines, cement plants, the iron and steel industry, etc.

Chemical Composition
C Mn Cr Mo S max P max
0.13 1.2 0.5 0.25 0.01 0.02

Applications
Quarries and Construction Earth Moving: Skimmers, crushers, screens, bunkers, bulldozers, etc.
Cement Plants: Buckets, crushers, bunkers, etc.
Mines, Coal mines: Excavator, winding and discharging machines, conveyors, etc.
Iron and steel industry: Bunkers, various casing, guide and shifting plates, etc.

Beyond-Steel Indonesia, distributor FORA 400 Indonesia jual FORA 400, ukuran FORA 400,harga FORA 400,diameter FORA 400,dia. FORA 400,beli FORA 400,distributor FORA 400,tebal FORA 400,berat FORA 400,pabrik FORA 400, stockist FORA 400,grade FORA 400, suplier FORA 400,chemical composition FORA 400, equivalent of FORA 400, mechanical properties FORA 400, physical properties FORA 400, properties of FORA 400, hrc FORA 400,thickness FORA 400, hardness FORA 400

Related Wear Plates:

Jembatan Gantung Terpanjang di Dunia

Rusia meresmikan jembatan gantung terpanjang di dunia pada 2 Juli, investasi bernilai triliunan rupiah ini berupaya untuk menghidupkan aktivitas ekonomi di kawasan Timur Jauh. Berikut gambar-gambarnya:

Sumber: AFP News